- 密度 [g/cm3]: 1.4
- 吸水率 [%]: 0.18
- 缺口沖擊強(qiáng)度: 1.87
- 斷裂伸長率 [%]: 234
- 彎曲強(qiáng)度 [MPa]: 165.0
- 彎曲模量 [MPa]: 9.00
- 硬度: 120.0
- 熱變形溫度 [℃]: 221.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in3 | ASTM D792 |
| Water Absorption | 0.18 % | 0.18 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 3.17 mm | 0.0020 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Ultimate | 165 MPa | 23900 psi | ASTM D638 |
| Elongation at Break | 3.0 - 4.0 % | 3.0 - 4.0 % | ASTM D638 |
| Flexural Yield Strength | 234 MPa | 33900 psi | ASTM D790 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ASTM D790 |
| Compressive Yield Strength | 160 MPa | 23200 psi | ASTM D695 |
| Shear Strength | 79.0 MPa | 11500 psi | ASTM D732 |
| Izod Impact, Notched | 1.87 J/cm @Thickness 6.35 mm | 3.50 ft-lb/in @Thickness 0.250 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 25.2 μm/m-°C @Temperature 20.0 °C | 14.0 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C | 421 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 271 - 293 °C | 520 - 559 °F | Stock |
| Mold Temperature | 93.0 - 107 °C | 199 - 225 °F | |
| Drying Temperature | 82.0 °C | 180 °F | |