- 密度 [g/cm3]: 1.31
- 吸水率 [%]: 4.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in3 | ISO 1183 | ||
| Water Absorption | 4.0 % | 4.0 % | ISO 62 | ||
| Moisture Absorption | 1.00 % | 1.00 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 120 MPa | 17400 psi | conditioned; ISO 2039-1 | ||
| 180 MPa | 26100 psi | dry; ISO 2039-1 | |||
| Tensile Strength at Break | 120 MPa | 17400 psi | conditioned; ISO 527-1/-2 | ||
| 155 MPa | 22500 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | 4.0 % | 4.0 % | dry; ISO 527-1/-2 | ||
| 6.0 % | 6.0 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 7.00 GPa | 1020 ksi | conditioned; ISO 527-1/-2 | ||
| 9.00 GPa | 1310 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | 9.50 J/cm2 | 45.2 ft-lb/in2 | dry; ISO 179/1eU | ||
| 9.50 J/cm2 | 45.2 ft-lb/in2 | conditioned; ISO 179/1eU | |||
| 9.00 J/cm2 @Temperature 30.0 °C | 42.8 ft-lb/in2 @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 9.00 J/cm2 @Temperature 30.0 °C | 42.8 ft-lb/in2 @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.60 J/cm2 | 7.61 ft-lb/in2 | conditioned; ISO 179/1eA | ||
| 1.80 J/cm2 | 8.57 ft-lb/in2 | dry; ISO 179/1eA | |||
| 1.10 J/cm2 @Temperature 30.0 °C | 5.23 ft-lb/in2 @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 1.10 J/cm2 @Temperature 30.0 °C | 5.23 ft-lb/in2 @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | dry; IEC 60093 | ||
| 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | conditioned; IEC 60093 | |||
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | IEC 60093 | ||
| Dielectric Strength | 45.0 kV/mm | 1140 kV/in | dry; IEC 60243-1 | ||
| 45.0 kV/mm | 1140 kV/in | conditioned; IEC 60243-1 | |||
| Comparative Tracking Index | 600 V | 600 V | conditioned; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 25.0 μm/m-°C | 13.9 μin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 80.0 μm/m-°C | 44.4 μin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 100 - 130 °C | 212 - 266 °F | long term; EMS | ||
| 160 °C | 320 °F | short term; EMS | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 120 °C | 248 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Automotive | Air intake sytems | ||||
| Automotive electr. and electronics, lighting | |||||
| Compressed air systems | |||||
| Cooling and climate control | |||||
| Fuel systems | |||||
| Hydraulic systems | |||||
| Form | Granules | ||||
| Industry & Consumer goods | Housewares | ||||
| Hydraulics & Pneumatics | |||||
| Mechanical Engineering | |||||
| Power transmission | |||||
| Processing | Injection Molding | ||||
| Product Attributes | Bio based Polyamide | ||||
| Special Characteristics | High impact or impact modified | ||||
| Improved heat resistance | |||||