- 缺口沖擊強度: 1.1
- 拉伸強度 [MPa]: 165.0
- 彎曲模量 [MPa]: 11.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | ASTM D792 | ||
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 165 MPa | 23900 psi | Type I, 5.1 mm/min; ASTM D638 | ||
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5.1 mm/min; ASTM D638 | ||
| Tensile Modulus | 11.0 GPa | 1600 ksi | Type I, 5.1 mm/min; ASTM D638 | ||
| Flexural Strength | 255 MPa | 37000 psi | ASTM D790 | ||
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 | ||
| Izod Impact, Notched | 1.10 J/cm @Thickness 3.18 mm, Temperature 23.0 °C | 2.06 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Injection Molded; ASTM D256A | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 249 - 271 °C | 480 - 520 °F | |||
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |||
| Drying Temperature | 71.1 - 82.2 °C | 160 - 180 °F | |||
| Dry Time | 2.00 hour | 2.00 hour | |||
| Descriptive Properties | |||||
| Features | Good Wear Resistance | ||||
| Forms | Pellets | ||||
| Generic Material | Nylon 610 | ||||
| Generic Name | Polyamide 610 (Nylon 610) | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Uses | Appliance Components | ||||
| Conveyor Parts | |||||
| Printer Parts | |||||