- 密度 [g/cm3]: 1.31
- 吸水率 [%]: 0.8
- 拉伸強(qiáng)度 [MPa]: 150.0
- 熱變形溫度 [℃]: 221.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in3 | ISO 1183 |
| Water Absorption | 0.80 % | 0.80 % | ISO 62 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | normal; ISO 294-4,2577 |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm | 0.010 in/in | parallel; ISO 294-4,2577 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 150 MPa | 21800 psi | ISO 527-2/1A |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527-2/1A |
| Tensile Modulus | 8.30 GPa | 1200 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 8.90 J/cm2 @Temperature -30.0 °C | 42.4 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU |
| 9.00 J/cm2 @Temperature 23.0 °C | 42.8 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm2 @Temperature -30.0 °C | 4.76 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA |
| 1.60 J/cm2 @Temperature 23.0 °C | 7.61 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ISO 60695 |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 222 °C | 432 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | ISO 75-1/2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1/2 |
| Vicat Softening Point | 217 °C | 423 °F | ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC60695 |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 - 300 °C | 500 - 572 °F | |
| Mold Temperature | 60.0 - 110 °C | 140 - 230 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 70.0 - 130 MPa | 10200 - 18900 psi | |