- 密度 [g/cm3]: 1.08
- 吸水率 [%]: 1.4
- 拉伸強度 [MPa]: 52.0
- 彎曲模量 [MPa]: 1.70
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in3 | ISO 1183 |
| Water Absorption | 1.4 % | 1.4 % | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | ISO 527-1/-2 |
| Elongation at Break | >= 50 % | >= 50 % | ISO 527-2/1A |
| Tensile Modulus | 2.00 GPa | 290 ksi | ISO 527-1/-2 |
| Flexural Modulus | 1.70 GPa | 247 ksi | ISO 178 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.600 J/cm2 @Temperature -30.0 °C | 2.86 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA |
| 0.800 J/cm2 @Temperature 23.0 °C | 3.81 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 222 °C | 432 °F | ISO 11357-3 |