- 密度 [g/cm3]: 1.13
- 缺口沖擊強度: 0.42
- 彎曲模量 [MPa]: 2.99
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm @Time 86400 sec | 0.015 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 73.0 MPa | 10600 psi | ASTM D638 |
| Elongation at Break | 7.2 % | 7.2 % | ASTM D638 |
| Tensile Modulus | 3.15 GPa | 457 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| Flexural Modulus | 2.99 GPa | 434 ksi | ASTM D790 |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.41 J/cm | 8.26 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 109 °C @Thickness 3.20 mm | 228 °F @Thickness 0.126 in | unannealed; ASTM D648 |