- 密度 [g/cm3]: 1.18
- 缺口沖擊強度: 0.27
- 彎曲模量 [MPa]: 2.43
- 熱變形溫度 [℃]: 161.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D 792 |
| Density | 1.18 g/cc | 0.0426 lb/in3 | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.29 % | 0.29 % | 23°C / 50% RH; ISO 62 |
| 0.20 % @Time 86400 sec | 0.20 % @Time 24.0 hour | 50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.010 - 0.030 cm/cm @Time 86400 sec | 0.010 - 0.030 in/in @Time 24.0 hour | ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.040 cm/cm @Time 86400 sec | 0.020 - 0.040 in/in @Time 24.0 hour | ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 66.0 MPa | 9570 psi | 5 mm/min; ISO 527 |
| 67.0 MPa | 9720 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 8.5 % | 8.5 % | 5 mm/min; ISO 527 |
| 10.2 % | 10.2 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 9.3 % | 9.3 % | Type I, 5 mm/min; ASTM D 638 |
| Tensile Modulus | 3.04 GPa | 441 ksi | 50 mm/min; ASTM D 638 |
| 3.07 GPa | 445 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 82.0 MPa | 11900 psi | ISO 178 |
| Flexural Modulus | 2.43 GPa | 352 ksi | 2 mm/min; ISO 178 |
| 2.67 GPa | 387 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.270 J/cm @Temperature 23.0 °C | 0.506 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 4.86 J/cm @Temperature 23.0 °C | 9.10 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m2 @Temperature 23.0 °C | 1.43 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m2 @Temperature 23.0 °C | 16.7 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1U |
| Impact Test | 2.00 J @Temperature 23.0 °C | 1.48 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D 257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 102 μm/m-°C @Temperature -30.0 - 30.0 °C | 56.7 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D 696 |
| CTE, linear, Transverse to Flow | 119 μm/m-°C @Temperature -30.0 - 30.0 °C | 66.1 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 161 °C | 322 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 180 °C @Thickness 3.20 mm | 356 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 92.0 °C @Thickness 3.20 mm | 198 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |