- 密度 [g/cm3]: 1.19
- 缺口沖擊強度: 1.27
- 拉伸強度 [MPa]: 92.0
- 彎曲模量 [MPa]: 4.48
- 熱變形溫度 [℃]: 170.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D 792 |
| Density | 1.19 g/cc | 0.0430 lb/in3 | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C / 50% RH; ISO 62 |
| 0.15 % @Time 86400 sec | 0.15 % @Time 24.0 hour | 50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm @Time 86400 sec | 0.0030 - 0.0060 in/in @Time 24.0 hour | ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.020 cm/cm @Time 86400 sec | 0.0090 - 0.020 in/in @Time 24.0 hour | ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 86.0 MPa | 12500 psi | Type I, 5 mm/min; ASTM D 638 |
| 91.0 MPa | 13200 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 92.0 MPa | 13300 psi | 5 mm/min; ISO 527 |
| 93.0 MPa | 13500 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 6.1 % | 6.1 % | Type I, 5 mm/min; ASTM D 638 |
| 6.3 % | 6.3 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 4.9 % | 4.9 % | Type I, 5 mm/min; ASTM D 638 |
| 4.9 % | 4.9 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 5.41 GPa | 785 ksi | 50 mm/min; ASTM D 638 |
| 5.41 GPa | 785 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 136 MPa | 19700 psi | ISO 178 |
| Flexural Modulus | 4.48 GPa | 650 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 4.72 GPa | 685 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.27 J/cm @Temperature 23.0 °C | 2.38 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 8.70 J/cm @Temperature 23.0 °C | 16.3 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m2 @Temperature 23.0 °C | 4.76 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 58.0 kJ/m2 @Temperature 23.0 °C | 27.6 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1U |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| 16.0 J @Temperature 23.0 °C | 11.8 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 | |
| Coefficient of Friction, Dynamic | 0.48 | 0.48 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.47 | 0.47 | ASTM D 3702 Modified |
| K (wear) Factor | 14.1 x 10-8 mm3/N-M | 7.00 x 10-10 in3-min/ft-lb-hr | Ring; ASTM D 3702 Modified |
| 103 x 10-8 mm3/N-M | 51.0 x 10-10 in3-min/ft-lb-hr | Washer; ASTM D 3702 Modified | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 40.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 22.2 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 175 °C @Thickness 3.20 mm | 347 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 161 °C @Thickness 3.20 mm | 322 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |