- 密度 [g/cm3]: 1.16
- 缺口沖擊強(qiáng)度: 0.3
- 拉伸強(qiáng)度 [MPa]: 43.0
- 彎曲模量 [MPa]: 1.87
- 熱變形溫度 [℃]: 146.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D 792 |
| Density | 1.16 g/cc | 0.0419 lb/in3 | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.020 % | 0.020 % | 23°C / 50% RH; ISO 62 |
| 0.020 % @Time 86400 sec | 0.020 % @Time 24.0 hour | 50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.010 - 0.030 cm/cm @Time 86400 sec | 0.010 - 0.030 in/in @Time 24.0 hour | ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec | 0.010 - 0.030 in/in @Time 24.0 hour | ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 43.0 MPa | 6240 psi | 5 mm/min; ISO 527 |
| 44.0 MPa | 6380 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | 5 mm/min; ISO 527 |
| 44.0 MPa | 6380 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 13.7 % | 13.7 % | 5 mm/min; ISO 527 |
| 17.5 % | 17.5 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 13.7 % | 13.7 % | 5 mm/min; ISO 527 |
| 17.3 % | 17.3 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 1.96 GPa | 284 ksi | 1 mm/min; ISO 527 |
| 2.02 GPa | 293 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 62.0 MPa | 8990 psi | ISO 178 |
| Flexural Modulus | 1.87 GPa | 271 ksi | 2 mm/min; ISO 178 |
| 1.91 GPa | 277 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.300 J/cm @Temperature 23.0 °C | 0.562 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 5.59 J/cm @Temperature 23.0 °C | 10.5 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m2 @Temperature 23.0 °C | 1.43 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 28.0 kJ/m2 @Temperature 23.0 °C | 13.3 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1U |
| Impact Test | 1.00 J @Temperature 23.0 °C | 0.738 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 |
| Coefficient of Friction, Dynamic | 0.21 | 0.21 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.11 | 0.11 | ASTM D 3702 Modified |
| K (wear) Factor | 22.2 x 10-8 mm3/N-M | 11.0 x 10-10 in3-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 112 μm/m-°C @Temperature -30.0 - 30.0 °C | 62.2 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D 696 |
| CTE, linear, Transverse to Flow | 127 μm/m-°C @Temperature -30.0 - 30.0 °C | 70.6 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 146 °C | 295 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 156 °C @Thickness 3.20 mm | 313 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 54.0 °C @Thickness 3.20 mm | 129 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |