- 密度 [g/cm3]: 1.21
- 缺口沖擊強度: 0.74
- 彎曲模量 [MPa]: 5.66
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Time 86400 sec | 0.0040 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 123 MPa | 17800 psi | ASTM D638 |
| Elongation at Break | 3.6 % | 3.6 % | ASTM D638 |
| Tensile Modulus | 5.90 GPa | 856 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 186 MPa | 27000 psi | ASTM D790 |
| Flexural Modulus | 5.66 GPa | 821 ksi | ASTM D790 |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.23 J/cm | 15.4 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C @Thickness 3.20 mm | 387 °F @Thickness 0.126 in | unannealed; ASTM D648 |