- 缺口沖擊強度: 0.32
- 彎曲模量 [MPa]: 9.25
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Moisture Absorption | 0.120 % | 0.120 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0089 cm/cm @Time 86400 sec | 0.0089 in/in @Time 24.0 hour | ISO 294 |
| 0.0090 cm/cm @Time 86400 sec | 0.0090 in/in @Time 24.0 hour | ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0145 cm/cm @Time 86400 sec | 0.0145 in/in @Time 24.0 hour | ISO 294 |
| 0.015 cm/cm @Time 86400 sec | 0.015 in/in @Time 24.0 hour | ASTM D955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 79.0 MPa | 11500 psi | ASTM D638 |
| 80.0 MPa | 11600 psi | ISO 527 | |
| Elongation at Break | 2.1 % | 2.1 % | ASTM D638 |
| 2.2 % | 2.2 % | ISO 527 | |
| Tensile Modulus | 9.98 GPa | 1450 ksi | 50 mm/min; ASTM D638 |
| 10.2 GPa | 1480 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 144 MPa | 20900 psi | ASTM D790 |
| 144 MPa | 20900 psi | ISO 178 | |
| Flexural Modulus | 9.25 GPa | 1340 ksi | ASTM D790 |
| 9.50 GPa | 1380 ksi | ISO 178 | |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.21 J/cm | 7.89 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m2 | 1.90 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 28.0 kJ/m2 | 13.3 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 1.10 W/m-K | 7.63 BTU-in/hr-ft2-°F | ASTM E 1530 |
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 167 °C @Thickness 3.20 mm | 333 °F @Thickness 0.126 in | unannealed; ASTM D648 | |