- 拉伸強(qiáng)度 [MPa]: 62.0
- 熱變形溫度 [℃]: 135.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec | >= 0.020 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec | 0.010 - 0.030 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 100 % | 100 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 4.5 % | 4.5 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 2.39 GPa | 347 ksi | 1 mm/min; ISO 527 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | ASTM D257 |
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz | 3.2 @Frequency 1.00e+6 Hz | ASTM D150 |
| 3.6 @Frequency 100 Hz | 3.6 @Frequency 100 Hz | ASTM D150 | |
| Dissipation Factor | 0.014 @Frequency 100000 Hz | 0.014 @Frequency 100000 Hz | ASTM D150 |
| 0.020 @Frequency 100 Hz | 0.020 @Frequency 100 Hz | ASTM D150 | |
| 0.020 @Frequency 1000 Hz | 0.020 @Frequency 1000 Hz | ASTM D150 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.0 °C | 144 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 55.0 °C @Thickness 3.20 mm | 131 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Oxygen Index | 27 % | 27 % | ISO 4589 |