- 密度 [g/cm3]: 1.17
- 拉伸強度 [MPa]: 53.0
- 熱變形溫度 [℃]: 186.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in3 | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 47.0 MPa | 6820 psi | ISO 527-2/1A |
| Tensile Strength, Yield | 53.0 MPa | 7690 psi | ISO 527-2/1A |
| Elongation at Break | 23 % | 23 % | ISO 527-2/1A |
| Elongation at Yield | 12 % | 12 % | ISO 527-2/1A |
| Tensile Modulus | 2.65 GPa | 384 ksi | ISO 527-2/1A |
| Charpy Impact Unnotched | 4.80 J/cm2 @Temperature -30.0 °C | 22.8 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU |
| 9.60 J/cm2 @Temperature 23.0 °C | 45.7 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.300 J/cm2 @Temperature -30.0 °C | 1.43 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA |
| 0.500 J/cm2 @Temperature 23.0 °C | 2.38 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 215 °C | 419 °F | Peak Temperature; ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 186 °C | 367 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 114 °C | 237 °F | ISO 75 |
| Vicat Softening Point | 193 °C | 379 °F | 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |