- 密度 [g/cm3]: 1.19
- 拉伸強度 [MPa]: 90.0
- 熱變形溫度 [℃]: 208.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in3 | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 86.0 MPa | 12500 psi | ISO 527-2/1A |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | ISO 527-2/1A |
| Elongation at Break | 10 % | 10 % | ISO 527-2/1A |
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527-2/1A |
| Tensile Modulus | 4.70 GPa | 682 ksi | ISO 527-2/1A |
| Charpy Impact Unnotched | 9.30 J/cm2 @Temperature 23.0 °C | 44.3 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU |
| 10.2 J/cm2 @Temperature -30.0 °C | 48.5 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 1.10 J/cm2 @Temperature -30.0 °C | 5.24 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA |
| 1.90 J/cm2 @Temperature 23.0 °C | 9.04 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 215 °C | 419 °F | Peak Temperature; ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 208 °C | 406 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 189 °C | 372 °F | ISO 75 |
| Vicat Softening Point | 207 °C | 405 °F | 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |