- 密度 [g/cm3]: 1.12
- 拉伸強度 [MPa]: 67.0
- 熱變形溫度 [℃]: 201.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in3 | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 62.0 MPa | 8990 psi | ISO 527-2/1A |
| Tensile Strength, Yield | 67.0 MPa | 9720 psi | ISO 527-2/1A |
| Elongation at Break | 12 % | 12 % | ISO 527-2/1A |
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527-2/1A |
| Tensile Modulus | 3.10 GPa | 450 ksi | ISO 527-2/1A |
| Charpy Impact Unnotched | 8.40 J/cm2 @Temperature -30.0 °C | 40.0 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU |
| 8.50 J/cm2 @Temperature 23.0 °C | 40.5 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.500 J/cm2 @Temperature -30.0 °C | 2.38 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA |
| 1.20 J/cm2 @Temperature 23.0 °C | 5.71 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 215 °C | 419 °F | Peak Temperature; ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 201 °C | 394 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 183 °C | 361 °F | ISO 75 |
| Vicat Softening Point | 199 °C | 390 °F | 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |