- 密度 [g/cm3]: 1.09
- 吸水率 [%]: 2.7
- 熱變形溫度 [℃]: 185.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in3 | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.0 % | 1.0 % | 23°C/50% R.H.; ISO 62 |
| Water Absorption at Saturation | 2.7 % | 2.7 % | ISO 62 |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | 127x12.7x3.2 mm (processing cond. acc. To DIN EN ISO 1874-2) |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | 127x12.7x3.2 mm (processing cond. acc. To DIN EN ISO 1874-2) |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 65.0 MPa | 9430 psi | ISO 527-2/1A |
| Elongation at Break | 7.0 % | 7.0 % | ISO 527-2/1A |
| Tensile Modulus | 2.65 GPa | 384 ksi | ISO 527-2/1A |
| Charpy Impact Unnotched | 11.0 J/cm2 @Temperature -30.0 °C | 52.4 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU |
| 11.5 J/cm2 @Temperature 23.0 °C | 54.7 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.300 J/cm2 @Temperature -30.0 °C | 1.43 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA |
| 0.400 J/cm2 @Temperature 23.0 °C | 1.90 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 130 μm/m-°C @Temperature 23.0 - 55.0 °C | 72.2 μin/in-°F @Temperature 73.4 - 131 °F | Longitudinal; ISO 11359 |
| CTE, linear, Transverse to Flow | 110 μm/m-°C @Temperature 23.0 - 55.0 °C | 61.1 μin/in-°F @Temperature 73.4 - 131 °F | ISO 11359 |
| Melting Point | 215 °C | 419 °F | Peak Temperature; ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 185 °C | 365 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75 |
| Vicat Softening Point | 187 °C | 369 °F | 50N; ISO 306 |