- 密度 [g/cm3]: 1.06
- 吸水率 [%]: 0.37
- 缺口沖擊強(qiáng)度: 0.64
- 拉伸強(qiáng)度 [MPa]: 46.0
- 彎曲模量 [MPa]: 2.30
- 熱變形溫度 [℃]: 155.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in3 | ASTM D792 |
| Water Absorption | 0.37 % | 0.37 % | 24 hrs; ASTM D570 |
| Water Absorption at Saturation | 2.8 % | 2.8 % | ASTM D570 |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | ASTM D638 |
| Elongation at Break | 250 % | 250 % | ASTM D638 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ASTM D790 |
| Izod Impact, Notched | 0.640 J/cm | 1.20 ft-lb/in | ASTM D256 |
| 0.500 J/cm @Temperature -40.0 °C | 0.937 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 50.0 μm/m-°C @Temperature 20.0 °C | 27.8 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Melting Point | 219 °C | 426 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |
- 關(guān)鍵詞:
- 供應(yīng)
- PA612
- Ashley Polymers Ashlene? 982 Nylon 612