- 密度 [g/cm3]: 1.17
- 吸水率 [%]: 2.4
- 拉伸強度 [MPa]: 63.0
- 熱變形溫度 [℃]: 186.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in3 | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.90 % | 0.90 % | 23°C/50% R.H.; ISO 62 |
| Water Absorption at Saturation | 2.4 % | 2.4 % | ISO 62 |
| Linear Mold Shrinkage | 0.0192 cm/cm | 0.0192 in/in | 127x12.7x3.2 mm (processing cond. acc. To DIN EN ISO 1874-2) |
| Linear Mold Shrinkage, Transverse | 0.0093 cm/cm | 0.0093 in/in | 127x12.7x3.2 mm (processing cond. acc. To DIN EN ISO 1874-2) |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 59.0 MPa | 8560 psi | ISO 527-2/1A |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | ISO 527-2/1A |
| Elongation at Break | 18 % | 18 % | ISO 527-2/1A |
| Elongation at Yield | 8.0 % | 8.0 % | ISO 527-2/1A |
| Tensile Modulus | 3.05 GPa | 442 ksi | ISO 527-2/1A |
| Charpy Impact Unnotched | 4.30 J/cm2 @Temperature -30.0 °C | 20.5 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU |
| 4.60 J/cm2 @Temperature 23.0 °C | 21.9 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.300 J/cm2 @Temperature -30.0 °C | 1.43 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA |
| 0.400 J/cm2 @Temperature 23.0 °C | 1.90 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.1 @Frequency 1e+6 Hz | 3.1 @Frequency 1e+6 Hz | IEC 60250 |
| 4.3 @Frequency 100 Hz | 4.3 @Frequency 100 Hz | IEC 60250 | |
| Dissipation Factor | 0.043 @Frequency 100 Hz | 0.043 @Frequency 100 Hz | IEC 60250 |
| 0.0493 @Frequency 1e+6 Hz | 0.0493 @Frequency 1e+6 Hz | IEC 60250 | |
| Comparative Tracking Index | 575 V | 575 V | Test Solution A, 100 drops; IEC 60112 |
| >= 600 V | >= 600 V | Test Solution A, 50 drops; IEC 60112 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 100 μm/m-°C @Temperature 23.0 - 55.0 °C | 55.6 μin/in-°F @Temperature 73.4 - 131 °F | Longitudinal; ISO 11359 |
| CTE, linear, Transverse to Flow | 60.0 μm/m-°C @Temperature 23.0 - 55.0 °C | 33.3 μin/in-°F @Temperature 73.4 - 131 °F | ISO 11359 |
| Melting Point | 215 °C | 419 °F | Peak Temperature; ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 186 °C | 367 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 114 °C | 237 °F | ISO 75 |
| Vicat Softening Point | 193 °C | 379 °F | 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |