- 密度 [g/cm3]: 1.06
- 吸水率 [%]: 0.37
- 缺口沖擊強(qiáng)度: 0.64
- 彎曲強(qiáng)度 [MPa]: 61.0
- 彎曲模量 [MPa]: 1.90
- 硬度: 115.0
- 熱變形溫度 [℃]: 164.0
- 脆化溫度 [℃]: -126.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in3 | ASTM D792 |
| Water Absorption | 0.37 % | 0.37 % | 24 hrs; ASTM D570 |
| Water Absorption at Saturation | 3.0 % | 3.0 % | ASTM D570 |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Ultimate | 61.0 MPa | 8850 psi | ATSM D638 |
| Elongation at Break | 90 % | 90 % | ASTM D638 |
| Flexural Modulus | 1.90 GPa | 276 ksi | ASTM D790 |
| Izod Impact, Notched | 0.640 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.5 @Frequency 1e+6 Hz | 3.5 @Frequency 1e+6 Hz | ASTM D150 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz | 0.020 @Frequency 1e+6 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 213 °C | 415 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 164 °C | 327 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ASTM D648 |
| Brittleness Temperature | -126 °C | -195 °F | ASTM D746 |
- 關(guān)鍵詞:
- 供應(yīng)
- PA612
- Ashley Polymers Ashlene? 981S Nylon 612