- 密度 [g/cm3]: 1.44
- 缺口沖擊強度: 1.25
- 拉伸強度 [MPa]: 145.0
- 斷裂伸長率 [%]: 229
- 彎曲模量 [MPa]: 8.87
- 熱變形溫度 [℃]: 214.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Density | 1.44 g/cc | 0.0520 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.190 % | 0.190 % | 50% RH, 24 hrs; ASTM D570 |
| 0.280 % | 0.280 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec | 0.0010 - 0.0030 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec | 0.010 - 0.030 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 145 MPa | 21000 psi | Type I, 5 mm/min; ASTM D638 |
| 146 MPa | 21200 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 145 MPa | 21000 psi | Type I, 5 mm/min; ASTM D638 |
| 146 MPa | 21200 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.7 % | 2.7 % | 5 mm/min; ISO 527 |
| 2.7 % | 2.7 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.7 % | 2.7 % | 5 mm/min; ISO 527 |
| 2.7 % | 2.7 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 9.69 GPa | 1410 ksi | 50 mm/min; ASTM D638 |
| 9.72 GPa | 1410 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 225 MPa | 32600 psi | ISO 178 |
| 229 MPa | 33200 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 229 MPa | 33200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 8.87 GPa | 1290 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 8.94 GPa | 1300 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.25 J/cm | 2.34 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.4 J/cm | 19.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m2 | 5.71 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 60.0 kJ/m2 | 28.6 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.62 | 0.62 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.52 | 0.52 | ASTM D3702 Modified |
| K (wear) Factor | 2.01 x 10-8 mm3/N-M | 1.00 x 10-10 in3-min/ft-lb-hr | Ring; ASTM D3702 Modified |
| 24.2 x 10-8 mm3/N-M | 12.0 x 10-10 in3-min/ft-lb-hr | Washer; ASTM D3702 Modified | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 14.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 7.78 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 75.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 41.7 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 214 °C @Thickness 3.20 mm | 417 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 200 °C @Thickness 3.20 mm | 392 °F @Thickness 0.126 in | unannealed; ASTM D648 | |