- 密度 [g/cm3]: 1.43
- 缺口沖擊強度: 1.03
- 斷裂伸長率 [%]: 193
- 彎曲模量 [MPa]: 7.41
- 熱變形溫度 [℃]: 211.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in3 | ISO 1183 |
| 1.44 g/cc | 0.0520 lb/in3 | ASTM D792 | |
| Moisture Absorption | 0.130 % | 0.130 % | 50% RH, 24 hrs; ASTM D570 |
| 0.180 % | 0.180 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec | 0.0040 - 0.0060 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec | 0.010 - 0.030 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 124 MPa | 18000 psi | 5 mm/min; ISO 527 |
| 127 MPa | 18400 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 |
| 2.8 % | 2.8 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 8.69 GPa | 1260 ksi | 1 mm/min; ISO 527 |
| 9.40 GPa | 1360 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 189 MPa | 27400 psi | ISO 178 |
| 192 MPa | 27800 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 193 MPa | 28000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 7.41 GPa | 1070 ksi | 2 mm/min; ISO 178 |
| 7.91 GPa | 1150 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.03 J/cm | 1.93 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.49 J/cm | 15.9 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m2 | 4.76 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 48.0 kJ/m2 | 22.8 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C | 5.90 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.61 | 0.61 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.59 | 0.59 | ASTM D3702 Modified |
| K (wear) Factor | 6.04 x 10-8 mm3/N-M | 3.00 x 10-10 in3-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 31.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 17.2 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 98.5 μm/m-°C @Temperature -30.0 - 30.0 °C | 54.7 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 211 °C | 412 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 213 °C @Thickness 3.20 mm | 415 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 197 °C @Thickness 3.20 mm | 387 °F @Thickness 0.126 in | unannealed; ASTM D648 | |