- 吸水率 [%]: 0.24
- 缺口沖擊強(qiáng)度: 1.07
- 彎曲強(qiáng)度 [MPa]: 179.0
- 彎曲模量 [MPa]: 11.7
- 熱變形溫度 [℃]: 216.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Water Absorption | 0.24 % @Thickness 3.17 mm | 0.24 % @Thickness 0.125 in | 24 hr. Immersion; ASTM D570 |
| Water Absorption at Saturation | 2.2 % @Thickness 3.17 mm | 2.2 % @Thickness 0.125 in | Long-Term Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0030 cm/cm | 0.0020 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 179 MPa | 26000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 276 MPa | 40000 psi | ASTM D790 |
| Flexural Modulus | 11.7 GPa | 1700 ksi | ASTM D790 |
| Compressive Strength | 145 MPa | 21000 psi | ASTM D695 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 2.00 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Method A, Injection Molded; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 10000 ohm-cm | 10000 ohm-cm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 420 °F | Unannealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Unannealed, 0.125 in bars; ASTM D648 |