- 吸水率 [%]: 0.3
- 缺口沖擊強度: 0.587
- 彎曲強度 [MPa]: 42.1
- 彎曲模量 [MPa]: 2.41
- 熱變形溫度 [℃]: 207.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.278 g/cc | 1.278 g/cc | ASTM D792 | ||
| Water Absorption | 0.30 % | 0.30 % | 24 hr. Immersion; ASTM D570 | ||
| Linear Mold Shrinkage | 0.010 - 0.015 cm/cm | 0.010 - 0.015 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 42.1 MPa | 6100 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Elongation at Break | 5.0 % | 5.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Tensile Modulus | 2.59 GPa | 375 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Flexural Strength | 62.1 MPa | 9000 psi | ASTM D790 | ||
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.587 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 1.10 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Method A, Injection Molded; ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 | ||
| Surface Resistivity per Square | 1.00e+14 ohm | 1.00e+14 ohm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 63.0 μm/m-°C @Temperature 20.0 °C | 35.0 μin/in-°F @Temperature 68.0 °F | ASTM D696 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 207 °C | 405 °F | Annealed, 0.125 in bars; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | Annealed, 0.125 in bars; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 232 - 260 °C | 450 - 500 °F | Molding | ||
| Mold Temperature | 93.3 - 107 °C | 200 - 225 °F | |||
| Drying Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |||
| Dry Time | 2 hour | 2 hour | |||
| Descriptive Properties | |||||
| Product Form | Pellets | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.