- 密度 [g/cm3]: 1.06
- 吸水率 [%]: 1.3
- 缺口沖擊強度: 3.0
- 拉伸強度 [MPa]: 54.0
- 彎曲模量 [MPa]: 1.44
- 硬度: 114.0
- 熱變形溫度 [℃]: 135.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in3 | DAM; ISO 1183 | ||
| Water Absorption | 1.3 % @Temperature 23.0 °C | 1.3 % @Temperature 73.4 °F | DAM; Equilibrium 50%RH; ISO 62, Similar to | ||
| 3.0 % @Temperature 23.0 °C | 3.0 % @Temperature 73.4 °F | DAM; Saturation, immersed; ISO 62, Similar to | |||
| Linear Mold Shrinkage, Flow | 0.011 cm/cm @Thickness 3.20 mm | 0.011 in/in @Thickness 0.126 in | DAM | ||
| 0.013 cm/cm @Thickness 2.00 mm | 0.013 in/in @Thickness 0.0787 in | DAM; ISO 294-4 | |||
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Thickness 3.20 mm | 0.011 in/in @Thickness 0.126 in | DAM | ||
| 0.014 cm/cm @Thickness 2.00 mm | 0.014 in/in @Thickness 0.0787 in | DAM; ISO 294-4 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 114 | 114 | DAM; ISO 2039/2 | ||
| Tensile Strength, Yield | 54.0 MPa @Temperature 23.0 °C | 7830 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 62.0 MPa @Temperature 23.0 °C | 8990 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 17 % @Temperature 23.0 °C | 17 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Elongation at Yield | 4.5 % @Temperature 23.0 °C | 4.5 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 18 % @Temperature 23.0 °C | 18 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 1.70 GPa @Temperature 23.0 °C | 247 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 2.40 GPa @Temperature 23.0 °C | 348 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Modulus | 1.44 GPa @Temperature 23.0 °C | 209 ksi @Temperature 73.4 °F | 50%RH; ISO 178 | ||
| 2.10 GPa @Temperature 23.0 °C | 305 ksi @Temperature 73.4 °F | DAM; ISO 178 | |||
| Izod Impact, Notched (ISO) | 3.00 kJ/m2 @Temperature -30.0 °C | 1.43 ft-lb/in2 @Temperature -22.0 °F | 50%RH; ISO 180/1A | ||
| 4.00 kJ/m2 @Temperature 23.0 °C | 1.90 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| 4.50 kJ/m2 @Temperature 23.0 °C | 2.14 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| 4.50 kJ/m2 @Temperature -30.0 °C | 2.14 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 180/1A | |||
| Charpy Impact Unnotched | 4.00 J/cm2 @Temperature -30.0 °C | 19.0 ft-lb/in2 @Temperature -22.0 °F | 50%RH; ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | DAM; ISO 179/1eU | |||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.300 J/cm2 @Temperature -30.0 °C | 1.43 ft-lb/in2 @Temperature -22.0 °F | 50%RH; ISO 179/1eA | ||
| 0.350 J/cm2 @Temperature 23.0 °C | 1.67 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| 0.350 J/cm2 @Temperature -30.0 °C | 1.67 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 179/1eA | |||
| 0.400 J/cm2 @Temperature 23.0 °C | 1.90 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 90.0 μm/m-°C @Temperature -40.0 - 23.0 °C | 50.0 μin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | ||
| 110 μm/m-°C @Temperature 23.0 - 55.0 °C | 61.1 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 160 μm/m-°C @Temperature 55.0 - 160 °C | 88.9 μin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 90.0 μm/m-°C @Temperature -40.0 - 23.0 °C | 50.0 μin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | ||
| 120 μm/m-°C @Temperature 23.0 - 55.0 °C | 66.7 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 180 μm/m-°C @Temperature 55.0 - 160 °C | 100 μin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| Melting Point | 218 °C | 424 °F | DAM; 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 62.0 °C | 144 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 °C | 482 °F | DAM; optimum | ||
| 230 - 290 °C | 446 - 554 °F | DAM | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; Optimum | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM; Dehumidified Dryer | ||
| Moisture Content | <= 0.15 % | <= 0.15 % | DAM | ||
| Descriptive Properties | |||||
| Additive | Lubricated | ||||
| Appearance | Natural Color | ||||
| Features | Chemical Resistance, Good | ||||
| Dimensional Stability, Good | |||||
| Lubricated | |||||
| Moisture Absorption, Low | |||||
| Water Absorption | |||||
| Forms | Pellets | ||||
| Generic | Nylon 612 | ||||
| Material Status | Current | ||||
| Part Marking Code | >PA612< | ISO 11469 | |||
| Processing Method | Injection Molding | ||||
| Product Category | Special Control Resins | ||||
| Unreinforced Resins | |||||
| Region Available - Global | Yes | ||||
| Resin Identification | PA612 | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||
| Uses | Medical Applications | ||||