- 密度 [g/cm3]: 1.0
- 缺口沖擊強度: 13.0
- 拉伸強度 [MPa]: 28.0
- 熱變形溫度 [℃]: 85.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.00 g/cc | 0.0361 lb/in3 | DAM; ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0276 cm/cm | 0.0276 in/in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0111 cm/cm | 0.0111 in/in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Stress | 0.0200 MPa @Strain 0.000 %, Temperature 60.0 °C | 2.90 psi @Strain 0.000 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | ||
| 0.0300 MPa @Strain 0.000 %, Temperature 60.0 °C | 4.35 psi @Strain 0.000 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.0500 MPa @Strain 0.000 %, Temperature 90.0 °C | 7.25 psi @Strain 0.000 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 0.0500 MPa @Strain 0.000 %, Temperature 90.0 °C | 7.25 psi @Strain 0.000 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.0700 MPa @Strain 0.000 %, Temperature -40.0 °C | 10.2 psi @Strain 0.000 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.0700 MPa @Strain 0.000 %, Temperature 40.0 °C | 10.2 psi @Strain 0.000 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.0800 MPa @Strain 0.000 %, Temperature 120 °C | 11.6 psi @Strain 0.000 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.0900 MPa @Strain 0.000 %, Temperature 120 °C | 13.1 psi @Strain 0.000 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 0.0900 MPa @Strain 0.000 %, Temperature 40.0 °C | 13.1 psi @Strain 0.000 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 0.100 MPa @Strain 0.000 %, Temperature 150 °C | 14.5 psi @Strain 0.000 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 0.110 MPa @Strain 0.000 %, Temperature 150 °C | 16.0 psi @Strain 0.000 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.160 MPa @Strain 0.000 %, Temperature 23.0 °C | 23.2 psi @Strain 0.000 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.180 MPa @Strain 0.000 %, Temperature -40.0 °C | 26.1 psi @Strain 0.000 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 0.190 MPa @Strain 0.000 %, Temperature 0.000 °C | 27.6 psi @Strain 0.000 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 0.210 MPa @Strain 0.000 %, Temperature 0.000 °C | 30.5 psi @Strain 0.000 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.250 MPa @Strain 0.000 %, Temperature 23.0 °C | 36.3 psi @Strain 0.000 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 0.290 MPa @Strain 0.000 %, Temperature -20.0 °C | 42.1 psi @Strain 0.000 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.530 MPa @Strain 0.0300 %, Temperature -40.0 °C | 76.9 psi @Strain 0.0300 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 0.550 MPa @Strain 0.0900 %, Temperature 40.0 °C | 79.8 psi @Strain 0.0900 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.750 MPa @Strain 0.0300 %, Temperature -40.0 °C | 109 psi @Strain 0.0300 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.850 MPa @Strain 0.110 %, Temperature 40.0 °C | 123 psi @Strain 0.110 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 0.960 MPa @Strain 0.0900 %, Temperature 23.0 °C | 139 psi @Strain 0.0900 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.02 MPa @Strain 0.170 %, Temperature 40.0 °C | 148 psi @Strain 0.170 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.13 MPa @Strain 0.0800 %, Temperature 23.0 °C | 164 psi @Strain 0.0800 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 1.21 MPa @Strain 0.0800 %, Temperature 0.000 °C | 175 psi @Strain 0.0800 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 1.33 MPa @Strain 0.0600 %, Temperature -20.0 °C | 193 psi @Strain 0.0600 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.39 MPa @Strain 0.0700 %, Temperature -40.0 °C | 202 psi @Strain 0.0700 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 1.39 MPa @Strain 0.0700 %, Temperature 0.000 °C | 202 psi @Strain 0.0700 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.53 MPa @Strain 0.200 %, Temperature 40.0 °C | 222 psi @Strain 0.200 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 1.64 MPa @Strain 0.0800 %, Temperature -40.0 °C | 238 psi @Strain 0.0800 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.72 MPa @Strain 0.170 %, Temperature 23.0 °C | 249 psi @Strain 0.170 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 2.04 MPa @Strain 0.160 %, Temperature 23.0 °C | 296 psi @Strain 0.160 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 2.16 MPa @Strain 0.150 %, Temperature 0.000 °C | 313 psi @Strain 0.150 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 2.23 MPa @Strain 0.110 %, Temperature -40.0 °C | 323 psi @Strain 0.110 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 2.35 MPa @Strain 0.120 %, Temperature -20.0 °C | 341 psi @Strain 0.120 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 2.37 MPa @Strain 0.160 %, Temperature 0.000 °C | 344 psi @Strain 0.160 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 2.37 MPa @Strain 0.920 %, Temperature 90.0 °C | 344 psi @Strain 0.920 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 2.60 MPa @Strain 0.110 %, Temperature -40.0 °C | 377 psi @Strain 0.110 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 2.82 MPa @Strain 3.27 %, Temperature 150 °C | 409 psi @Strain 3.27 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 2.83 MPa @Strain 0.440 %, Temperature 40.0 °C | 410 psi @Strain 0.440 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 2.90 MPa @Strain 2.19 %, Temperature 120 °C | 421 psi @Strain 2.19 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 2.92 MPa @Strain 0.240 %, Temperature 23.0 °C | 424 psi @Strain 0.240 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 3.02 MPa @Strain 0.150 %, Temperature -40.0 °C | 438 psi @Strain 0.150 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 3.08 MPa @Strain 0.220 %, Temperature 0.000 °C | 447 psi @Strain 0.220 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 3.18 MPa @Strain 4.50 %, Temperature 150 °C | 461 psi @Strain 4.50 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 3.33 MPa @Strain 0.180 %, Temperature -20.0 °C | 483 psi @Strain 0.180 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 3.44 MPa @Strain 0.230 %, Temperature 0.000 °C | 499 psi @Strain 0.230 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 3.57 MPa @Strain 0.150 %, Temperature -40.0 °C | 518 psi @Strain 0.150 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 3.86 MPa @Strain 0.190 %, Temperature -40.0 °C | 560 psi @Strain 0.190 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 4.05 MPa @Strain 0.400 %, Temperature 23.0 °C | 587 psi @Strain 0.400 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 4.23 MPa @Strain 0.240 %, Temperature -20.0 °C | 614 psi @Strain 0.240 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 4.42 MPa @Strain 0.190 %, Temperature -40.0 °C | 641 psi @Strain 0.190 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 4.73 MPa @Strain 0.230 %, Temperature -40.0 °C | 686 psi @Strain 0.230 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 4.73 MPa @Strain 4.13 %, Temperature 120 °C | 686 psi @Strain 4.13 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 5.32 MPa @Strain 0.230 %, Temperature -40.0 °C | 772 psi @Strain 0.230 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 5.51 MPa @Strain 2.96 %, Temperature 90.0 °C | 799 psi @Strain 2.96 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 5.69 MPa @Strain 19.51 %, Temperature 150 °C | 825 psi @Strain 19.51 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 5.95 MPa @Strain 17.66 %, Temperature 150 °C | 863 psi @Strain 17.66 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 6.39 MPa @Strain 35.26 %, Temperature 150 °C | 927 psi @Strain 35.26 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 6.69 MPa @Strain 32.75 %, Temperature 150 °C | 970 psi @Strain 32.75 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 6.81 MPa @Strain 51.14 %, Temperature 150 °C | 988 psi @Strain 51.14 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 7.10 MPa @Strain 48.0 %, Temperature 150 °C | 1030 psi @Strain 48.0 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 7.14 MPa @Strain 66.88 %, Temperature 150 °C | 1040 psi @Strain 66.88 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 7.34 MPa @Strain 1.88 %, Temperature 60.0 °C | 1060 psi @Strain 1.88 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 7.41 MPa @Strain 63.26 %, Temperature 150 °C | 1070 psi @Strain 63.26 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 7.43 MPa @Strain 82.35 %, Temperature 150 °C | 1080 psi @Strain 82.35 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 7.67 MPa @Strain 78.3 %, Temperature 150 °C | 1110 psi @Strain 78.3 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 7.69 MPa @Strain 97.54 %, Temperature 150 °C | 1120 psi @Strain 97.54 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 7.75 MPa @Strain 15.98 %, Temperature 120 °C | 1120 psi @Strain 15.98 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 7.93 MPa @Strain 93.16 %, Temperature 150 °C | 1150 psi @Strain 93.16 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 7.95 MPa @Strain 112.41 %, Temperature 150 °C | 1150 psi @Strain 112.41 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 8.18 MPa @Strain 107.75 %, Temperature 150 °C | 1190 psi @Strain 107.75 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 8.23 MPa @Strain 126.89 %, Temperature 150 °C | 1190 psi @Strain 126.89 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 8.24 MPa @Strain 17.39 %, Temperature 120 °C | 1200 psi @Strain 17.39 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 8.42 MPa @Strain 122.15 %, Temperature 150 °C | 1220 psi @Strain 122.15 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 8.52 MPa @Strain 140.93 %, Temperature 150 °C | 1240 psi @Strain 140.93 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 8.69 MPa @Strain 136.16 %, Temperature 150 °C | 1260 psi @Strain 136.16 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 8.75 MPa @Strain 30.85 %, Temperature 120 °C | 1270 psi @Strain 30.85 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 8.82 MPa @Strain 154.53 %, Temperature 150 °C | 1280 psi @Strain 154.53 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 8.97 MPa @Strain 149.65 %, Temperature 150 °C | 1300 psi @Strain 149.65 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 9.12 MPa @Strain 31.5 %, Temperature 120 °C | 1320 psi @Strain 31.5 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 9.13 MPa @Strain 167.68 %, Temperature 150 °C | 1320 psi @Strain 167.68 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 9.27 MPa @Strain 162.84 %, Temperature 150 °C | 1340 psi @Strain 162.84 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 9.28 MPa @Strain 45.91 %, Temperature 120 °C | 1350 psi @Strain 45.91 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 9.44 MPa @Strain 180.47 %, Temperature 150 °C | 1370 psi @Strain 180.47 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 9.57 MPa @Strain 175.62 %, Temperature 150 °C | 1390 psi @Strain 175.62 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 9.62 MPa @Strain 45.81 %, Temperature 120 °C | 1400 psi @Strain 45.81 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 9.67 MPa @Strain 60.87 %, Temperature 120 °C | 1400 psi @Strain 60.87 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 9.77 MPa @Strain 192.86 %, Temperature 150 °C | 1420 psi @Strain 192.86 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 9.89 MPa @Strain 188.08 %, Temperature 150 °C | 1430 psi @Strain 188.08 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 9.98 MPa @Strain 75.62 %, Temperature 120 °C | 1450 psi @Strain 75.62 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 9.98 MPa @Strain 60.03 %, Temperature 120 °C | 1450 psi @Strain 60.03 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 10.11 MPa @Strain 205.16 %, Temperature 150 °C | 1466 psi @Strain 205.16 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 10.21 MPa @Strain 200.29 %, Temperature 150 °C | 1481 psi @Strain 200.29 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 10.3 MPa @Strain 74.13 %, Temperature 120 °C | 1490 psi @Strain 74.13 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 10.3 MPa @Strain 90.08 %, Temperature 120 °C | 1490 psi @Strain 90.08 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 10.46 MPa @Strain 217.24 %, Temperature 150 °C | 1517 psi @Strain 217.24 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 10.56 MPa @Strain 212.4 %, Temperature 150 °C | 1532 psi @Strain 212.4 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 10.56 MPa @Strain 87.95 %, Temperature 120 °C | 1532 psi @Strain 87.95 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 10.59 MPa @Strain 104.21 %, Temperature 120 °C | 1536 psi @Strain 104.21 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 10.81 MPa @Strain 229.23 %, Temperature 150 °C | 1568 psi @Strain 229.23 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 10.84 MPa @Strain 101.45 %, Temperature 120 °C | 1572 psi @Strain 101.45 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 10.88 MPa @Strain 118.11 %, Temperature 120 °C | 1578 psi @Strain 118.11 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 10.91 MPa @Strain 224.45 %, Temperature 150 °C | 1582 psi @Strain 224.45 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 11.1 MPa @Strain 114.65 %, Temperature 120 °C | 1610 psi @Strain 114.65 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 11.18 MPa @Strain 241.02 %, Temperature 150 °C | 1622 psi @Strain 241.02 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 11.19 MPa @Strain 131.66 %, Temperature 120 °C | 1623 psi @Strain 131.66 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 11.21 MPa @Strain 4.54 %, Temperature 60.0 °C | 1626 psi @Strain 4.54 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 11.26 MPa @Strain 236.28 %, Temperature 150 °C | 1633 psi @Strain 236.28 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 11.38 MPa @Strain 127.51 %, Temperature 120 °C | 1651 psi @Strain 127.51 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 11.48 MPa @Strain 144.92 %, Temperature 120 °C | 1665 psi @Strain 144.92 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 11.56 MPa @Strain 252.8 %, Temperature 150 °C | 1677 psi @Strain 252.8 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 11.64 MPa @Strain 248.09 %, Temperature 150 °C | 1688 psi @Strain 248.09 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 11.65 MPa @Strain 140.04 %, Temperature 120 °C | 1690 psi @Strain 140.04 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 11.7 MPa @Strain 12.45 %, Temperature 90.0 °C | 1700 psi @Strain 12.45 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 11.8 MPa @Strain 157.84 %, Temperature 120 °C | 1710 psi @Strain 157.84 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 11.8 MPa @Strain 16.87 %, Temperature 90.0 °C | 1710 psi @Strain 16.87 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 11.92 MPa @Strain 264.19 %, Temperature 150 °C | 1729 psi @Strain 264.19 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 11.94 MPa @Strain 152.3 %, Temperature 120 °C | 1732 psi @Strain 152.3 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 12.0 MPa @Strain 259.5 %, Temperature 150 °C | 1740 psi @Strain 259.5 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 12.14 MPa @Strain 170.48 %, Temperature 120 °C | 1761 psi @Strain 170.48 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 12.23 MPa @Strain 164.29 %, Temperature 120 °C | 1774 psi @Strain 164.29 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 12.28 MPa @Strain 274.97 %, Temperature 150 °C | 1781 psi @Strain 274.97 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 12.4 MPa @Strain 270.76 %, Temperature 150 °C | 1800 psi @Strain 270.76 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 12.47 MPa @Strain 182.84 %, Temperature 120 °C | 1809 psi @Strain 182.84 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 12.55 MPa @Strain 175.98 %, Temperature 120 °C | 1820 psi @Strain 175.98 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 12.64 MPa @Strain 285.05 %, Temperature 150 °C | 1833 psi @Strain 285.05 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 12.77 MPa @Strain 281.4 %, Temperature 150 °C | 1852 psi @Strain 281.4 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 12.83 MPa @Strain 194.84 %, Temperature 120 °C | 1861 psi @Strain 194.84 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 12.87 MPa @Strain 187.44 %, Temperature 120 °C | 1867 psi @Strain 187.44 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 12.9 MPa @Strain 299.65 %, Temperature 150 °C | 1870 psi @Strain 299.65 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 12.9 MPa @Strain 1.80 %, Temperature 40.0 °C | 1870 psi @Strain 1.80 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 13.04 MPa @Strain 294.52 %, Temperature 150 °C | 1891 psi @Strain 294.52 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 13.09 MPa @Strain 32.29 %, Temperature 90.0 °C | 1899 psi @Strain 32.29 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 13.13 MPa @Strain 296.43 %, Temperature 150 °C | 1904 psi @Strain 296.43 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 13.17 MPa @Strain 291.54 %, Temperature 150 °C | 1910 psi @Strain 291.54 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 13.17 MPa @Strain 206.68 %, Temperature 120 °C | 1910 psi @Strain 206.68 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 13.19 MPa @Strain 198.59 %, Temperature 120 °C | 1913 psi @Strain 198.59 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 13.45 MPa @Strain 25.47 %, Temperature 90.0 °C | 1951 psi @Strain 25.47 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 13.53 MPa @Strain 209.56 %, Temperature 120 °C | 1962 psi @Strain 209.56 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 13.56 MPa @Strain 218.34 %, Temperature 120 °C | 1967 psi @Strain 218.34 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 13.6 MPa @Strain 48.45 %, Temperature 90.0 °C | 1970 psi @Strain 48.45 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 13.71 MPa @Strain 0.600 %, Temperature -40.0 °C | 1988 psi @Strain 0.600 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 13.89 MPa @Strain 64.92 %, Temperature 90.0 °C | 2015 psi @Strain 64.92 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 13.89 MPa @Strain 220.36 %, Temperature 120 °C | 2015 psi @Strain 220.36 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 13.93 MPa @Strain 229.8 %, Temperature 120 °C | 2020 psi @Strain 229.8 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 14.12 MPa @Strain 39.22 %, Temperature 90.0 °C | 2048 psi @Strain 39.22 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 14.16 MPa @Strain 81.48 %, Temperature 90.0 °C | 2054 psi @Strain 81.48 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 14.26 MPa @Strain 231.11 %, Temperature 120 °C | 2068 psi @Strain 231.11 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 14.33 MPa @Strain 241.21 %, Temperature 120 °C | 2078 psi @Strain 241.21 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 14.43 MPa @Strain 97.84 %, Temperature 90.0 °C | 2093 psi @Strain 97.84 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 14.46 MPa @Strain 53.36 %, Temperature 90.0 °C | 2097 psi @Strain 53.36 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 14.62 MPa @Strain 241.81 %, Temperature 120 °C | 2120 psi @Strain 241.81 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 14.72 MPa @Strain 113.54 %, Temperature 90.0 °C | 2135 psi @Strain 113.54 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 14.72 MPa @Strain 67.68 %, Temperature 90.0 °C | 2135 psi @Strain 67.68 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 14.74 MPa @Strain 252.66 %, Temperature 120 °C | 2138 psi @Strain 252.66 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 14.93 MPa @Strain 0.710 %, Temperature -40.0 °C | 2165 psi @Strain 0.710 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 14.95 MPa @Strain 81.99 %, Temperature 90.0 °C | 2168 psi @Strain 81.99 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 15.02 MPa @Strain 252.47 %, Temperature 120 °C | 2178 psi @Strain 252.47 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 15.02 MPa @Strain 128.33 %, Temperature 90.0 °C | 2178 psi @Strain 128.33 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 15.03 MPa @Strain 3.85 %, Temperature 40.0 °C | 2180 psi @Strain 3.85 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 15.15 MPa @Strain 263.74 %, Temperature 120 °C | 2197 psi @Strain 263.74 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 15.19 MPa @Strain 96.12 %, Temperature 90.0 °C | 2203 psi @Strain 96.12 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 15.35 MPa @Strain 142.29 %, Temperature 90.0 °C | 2226 psi @Strain 142.29 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 15.41 MPa @Strain 263 %, Temperature 120 °C | 2235 psi @Strain 263 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 15.46 MPa @Strain 109.84 %, Temperature 90.0 °C | 2242 psi @Strain 109.84 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 15.56 MPa @Strain 274.47 %, Temperature 120 °C | 2257 psi @Strain 274.47 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 15.71 MPa @Strain 122.91 %, Temperature 90.0 °C | 2279 psi @Strain 122.91 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 15.72 MPa @Strain 155.6 %, Temperature 90.0 °C | 2280 psi @Strain 155.6 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 15.82 MPa @Strain 273.29 %, Temperature 120 °C | 2295 psi @Strain 273.29 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 15.99 MPa @Strain 285.08 %, Temperature 120 °C | 2319 psi @Strain 285.08 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 16.02 MPa @Strain 135.38 %, Temperature 90.0 °C | 2324 psi @Strain 135.38 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 16.11 MPa @Strain 168.66 %, Temperature 90.0 °C | 2337 psi @Strain 168.66 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 16.14 MPa @Strain 283.21 %, Temperature 120 °C | 2341 psi @Strain 283.21 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 16.21 MPa @Strain 294.78 %, Temperature 120 °C | 2351 psi @Strain 294.78 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 16.31 MPa @Strain 147.19 %, Temperature 90.0 °C | 2366 psi @Strain 147.19 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 16.52 MPa @Strain 181.55 %, Temperature 90.0 °C | 2396 psi @Strain 181.55 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 16.65 MPa @Strain 158.56 %, Temperature 90.0 °C | 2415 psi @Strain 158.56 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 16.95 MPa @Strain 194.43 %, Temperature 90.0 °C | 2458 psi @Strain 194.43 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 16.99 MPa @Strain 169.69 %, Temperature 90.0 °C | 2464 psi @Strain 169.69 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 17.01 MPa @Strain 19.15 %, Temperature 60.0 °C | 2467 psi @Strain 19.15 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 17.14 MPa @Strain 13.0 %, Temperature 60.0 °C | 2486 psi @Strain 13.0 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 17.36 MPa @Strain 180.69 %, Temperature 90.0 °C | 2518 psi @Strain 180.69 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 17.41 MPa @Strain 207.24 %, Temperature 90.0 °C | 2525 psi @Strain 207.24 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 17.6 MPa @Strain 1.36 %, Temperature 0.000 °C | 2550 psi @Strain 1.36 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 17.77 MPa @Strain 191.56 %, Temperature 90.0 °C | 2577 psi @Strain 191.56 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 17.88 MPa @Strain 219.87 %, Temperature 90.0 °C | 2593 psi @Strain 219.87 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 18.04 MPa @Strain 35.26 %, Temperature 60.0 °C | 2616 psi @Strain 35.26 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 18.17 MPa @Strain 202.46 %, Temperature 90.0 °C | 2635 psi @Strain 202.46 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 18.29 MPa @Strain 52.4 %, Temperature 60.0 °C | 2653 psi @Strain 52.4 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 18.39 MPa @Strain 232.5 %, Temperature 90.0 °C | 2667 psi @Strain 232.5 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 18.44 MPa @Strain 70.13 %, Temperature 60.0 °C | 2675 psi @Strain 70.13 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 18.59 MPa @Strain 213.33 %, Temperature 90.0 °C | 2696 psi @Strain 213.33 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 18.63 MPa @Strain 88.02 %, Temperature 60.0 °C | 2702 psi @Strain 88.02 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 18.89 MPa @Strain 105.65 %, Temperature 60.0 °C | 2740 psi @Strain 105.65 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 18.9 MPa @Strain 244.94 %, Temperature 90.0 °C | 2740 psi @Strain 244.94 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 19.01 MPa @Strain 224.27 %, Temperature 90.0 °C | 2757 psi @Strain 224.27 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 19.01 MPa @Strain 7.56 %, Temperature 40.0 °C | 2757 psi @Strain 7.56 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 19.07 MPa @Strain 25.19 %, Temperature 60.0 °C | 2766 psi @Strain 25.19 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 19.19 MPa @Strain 122.44 %, Temperature 60.0 °C | 2783 psi @Strain 122.44 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 19.41 MPa @Strain 257.22 %, Temperature 90.0 °C | 2815 psi @Strain 257.22 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 19.44 MPa @Strain 235.21 %, Temperature 90.0 °C | 2820 psi @Strain 235.21 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 19.51 MPa @Strain 137.65 %, Temperature 60.0 °C | 2830 psi @Strain 137.65 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 19.75 MPa @Strain 37.87 %, Temperature 60.0 °C | 2865 psi @Strain 37.87 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 19.85 MPa @Strain 150.93 %, Temperature 60.0 °C | 2879 psi @Strain 150.93 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 19.89 MPa @Strain 245.98 %, Temperature 90.0 °C | 2885 psi @Strain 245.98 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 19.94 MPa @Strain 269.18 %, Temperature 90.0 °C | 2892 psi @Strain 269.18 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 20.02 MPa @Strain 50.88 %, Temperature 60.0 °C | 2904 psi @Strain 50.88 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 20.2 MPa @Strain 63.96 %, Temperature 60.0 °C | 2930 psi @Strain 63.96 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 20.25 MPa @Strain 162.73 %, Temperature 60.0 °C | 2937 psi @Strain 162.73 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 20.36 MPa @Strain 256.65 %, Temperature 90.0 °C | 2953 psi @Strain 256.65 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 20.4 MPa @Strain 77.07 %, Temperature 60.0 °C | 2960 psi @Strain 77.07 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 20.49 MPa @Strain 280.95 %, Temperature 90.0 °C | 2972 psi @Strain 280.95 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 20.63 MPa @Strain 90.3 %, Temperature 60.0 °C | 2992 psi @Strain 90.3 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 20.72 MPa @Strain 174.03 %, Temperature 60.0 °C | 3005 psi @Strain 174.03 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 20.82 MPa @Strain 267.18 %, Temperature 90.0 °C | 3020 psi @Strain 267.18 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 20.87 MPa @Strain 11.52 %, Temperature 40.0 °C | 3027 psi @Strain 11.52 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 20.89 MPa @Strain 103.68 %, Temperature 60.0 °C | 3030 psi @Strain 103.68 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 20.92 MPa @Strain 313.56 %, Temperature 90.0 °C | 3034 psi @Strain 313.56 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 20.97 MPa @Strain 2.95 %, Temperature 23.0 °C | 3041 psi @Strain 2.95 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 21.0 MPa @Strain 5.34 %, Temperature 40.0 °C | 3050 psi @Strain 5.34 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 21.04 MPa @Strain 292.45 %, Temperature 90.0 °C | 3052 psi @Strain 292.45 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 21.06 MPa @Strain 277.32 %, Temperature 90.0 °C | 3055 psi @Strain 277.32 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 21.15 MPa @Strain 117.28 %, Temperature 60.0 °C | 3068 psi @Strain 117.28 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 21.22 MPa @Strain 185.65 %, Temperature 60.0 °C | 3078 psi @Strain 185.65 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 21.45 MPa @Strain 130.83 %, Temperature 60.0 °C | 3111 psi @Strain 130.83 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 21.54 MPa @Strain 2.11 %, Temperature 23.0 °C | 3124 psi @Strain 2.11 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 21.63 MPa @Strain 303.65 %, Temperature 90.0 °C | 3137 psi @Strain 303.65 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 21.72 MPa @Strain 198.05 %, Temperature 60.0 °C | 3150 psi @Strain 198.05 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 21.74 MPa @Strain 144.06 %, Temperature 60.0 °C | 3153 psi @Strain 144.06 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 21.83 MPa @Strain 15.69 %, Temperature 40.0 °C | 3166 psi @Strain 15.69 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 22.0 MPa @Strain 156.52 %, Temperature 60.0 °C | 3190 psi @Strain 156.52 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 22.23 MPa @Strain 211.25 %, Temperature 60.0 °C | 3224 psi @Strain 211.25 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 22.32 MPa @Strain 167.93 %, Temperature 60.0 °C | 3237 psi @Strain 167.93 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 22.37 MPa @Strain 20.02 %, Temperature 40.0 °C | 3245 psi @Strain 20.02 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 22.55 MPa @Strain 68.63 %, Temperature 40.0 °C | 3271 psi @Strain 68.63 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 22.55 MPa @Strain 73.8 %, Temperature 40.0 °C | 3271 psi @Strain 73.8 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 22.58 MPa @Strain 78.98 %, Temperature 40.0 °C | 3275 psi @Strain 78.98 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 22.59 MPa @Strain 63.51 %, Temperature 40.0 °C | 3276 psi @Strain 63.51 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 22.6 MPa @Strain 84.17 %, Temperature 40.0 °C | 3280 psi @Strain 84.17 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 22.63 MPa @Strain 58.4 %, Temperature 40.0 °C | 3282 psi @Strain 58.4 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 22.64 MPa @Strain 89.43 %, Temperature 40.0 °C | 3284 psi @Strain 89.43 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 22.66 MPa @Strain 24.42 %, Temperature 40.0 °C | 3287 psi @Strain 24.42 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 22.68 MPa @Strain 53.34 %, Temperature 40.0 °C | 3289 psi @Strain 53.34 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 22.7 MPa @Strain 178.24 %, Temperature 60.0 °C | 3290 psi @Strain 178.24 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 22.71 MPa @Strain 94.73 %, Temperature 40.0 °C | 3294 psi @Strain 94.73 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 22.74 MPa @Strain 48.33 %, Temperature 40.0 °C | 3298 psi @Strain 48.33 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 22.77 MPa @Strain 224.9 %, Temperature 60.0 °C | 3303 psi @Strain 224.9 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 22.8 MPa @Strain 43.37 %, Temperature 40.0 °C | 3310 psi @Strain 43.37 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 22.8 MPa @Strain 100.04 %, Temperature 40.0 °C | 3310 psi @Strain 100.04 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 22.81 MPa @Strain 29.03 %, Temperature 40.0 °C | 3308 psi @Strain 29.03 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 22.85 MPa @Strain 33.72 %, Temperature 40.0 °C | 3314 psi @Strain 33.72 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 22.85 MPa @Strain 38.5 %, Temperature 40.0 °C | 3314 psi @Strain 38.5 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 23.1 MPa @Strain 187.84 %, Temperature 60.0 °C | 3350 psi @Strain 187.84 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 23.16 MPa @Strain 9.35 %, Temperature 40.0 °C | 3359 psi @Strain 9.35 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 23.34 MPa @Strain 238.58 %, Temperature 60.0 °C | 3385 psi @Strain 238.58 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 23.51 MPa @Strain 197.35 %, Temperature 60.0 °C | 3410 psi @Strain 197.35 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 23.93 MPa @Strain 207.11 %, Temperature 60.0 °C | 3471 psi @Strain 207.11 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 23.93 MPa @Strain 251.94 %, Temperature 60.0 °C | 3471 psi @Strain 251.94 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 24.23 MPa @Strain 13.55 %, Temperature 40.0 °C | 3514 psi @Strain 13.55 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 24.34 MPa @Strain 217.27 %, Temperature 60.0 °C | 3530 psi @Strain 217.27 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 24.54 MPa @Strain 264.68 %, Temperature 60.0 °C | 3559 psi @Strain 264.68 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 24.76 MPa @Strain 227.91 %, Temperature 60.0 °C | 3591 psi @Strain 227.91 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 24.84 MPa @Strain 17.81 %, Temperature 40.0 °C | 3603 psi @Strain 17.81 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 24.85 MPa @Strain 2.10 %, Temperature 0.000 °C | 3604 psi @Strain 2.10 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 25.05 MPa @Strain 75.46 %, Temperature 40.0 °C | 3633 psi @Strain 75.46 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 25.07 MPa @Strain 70.38 %, Temperature 40.0 °C | 3636 psi @Strain 70.38 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 25.08 MPa @Strain 80.52 %, Temperature 40.0 °C | 3638 psi @Strain 80.52 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 25.09 MPa @Strain 65.32 %, Temperature 40.0 °C | 3639 psi @Strain 65.32 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 25.14 MPa @Strain 85.69 %, Temperature 40.0 °C | 3646 psi @Strain 85.69 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 25.14 MPa @Strain 60.33 %, Temperature 40.0 °C | 3646 psi @Strain 60.33 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 25.18 MPa @Strain 276.85 %, Temperature 60.0 °C | 3652 psi @Strain 276.85 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 25.19 MPa @Strain 22.16 %, Temperature 40.0 °C | 3654 psi @Strain 22.16 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 25.2 MPa @Strain 90.87 %, Temperature 40.0 °C | 3650 psi @Strain 90.87 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 25.2 MPa @Strain 55.37 %, Temperature 40.0 °C | 3650 psi @Strain 55.37 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 25.22 MPa @Strain 238.91 %, Temperature 60.0 °C | 3658 psi @Strain 238.91 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 25.27 MPa @Strain 96.05 %, Temperature 40.0 °C | 3665 psi @Strain 96.05 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 25.28 MPa @Strain 50.42 %, Temperature 40.0 °C | 3667 psi @Strain 50.42 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 25.31 MPa @Strain 100.77 %, Temperature 40.0 °C | 3671 psi @Strain 100.77 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 25.35 MPa @Strain 45.53 %, Temperature 40.0 °C | 3677 psi @Strain 45.53 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 25.38 MPa @Strain 26.66 %, Temperature 40.0 °C | 3681 psi @Strain 26.66 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 25.41 MPa @Strain 40.72 %, Temperature 40.0 °C | 3685 psi @Strain 40.72 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 25.45 MPa @Strain 31.26 %, Temperature 40.0 °C | 3691 psi @Strain 31.26 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 25.45 MPa @Strain 35.92 %, Temperature 40.0 °C | 3691 psi @Strain 35.92 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 25.69 MPa @Strain 250.13 %, Temperature 60.0 °C | 3726 psi @Strain 250.13 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 25.82 MPa @Strain 288.57 %, Temperature 60.0 °C | 3745 psi @Strain 288.57 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 25.94 MPa @Strain 322.13 %, Temperature 60.0 °C | 3762 psi @Strain 322.13 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 26.08 MPa @Strain 271.73 %, Temperature 60.0 °C | 3783 psi @Strain 271.73 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 26.08 MPa @Strain 6.11 %, Temperature 23.0 °C | 3783 psi @Strain 6.11 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 26.16 MPa @Strain 261.32 %, Temperature 60.0 °C | 3794 psi @Strain 261.32 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 26.46 MPa @Strain 65.41 %, Temperature 23.0 °C | 3838 psi @Strain 65.41 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 26.47 MPa @Strain 71.19 %, Temperature 23.0 °C | 3839 psi @Strain 71.19 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 26.5 MPa @Strain 300.06 %, Temperature 60.0 °C | 3840 psi @Strain 300.06 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 26.55 MPa @Strain 76.97 %, Temperature 23.0 °C | 3851 psi @Strain 76.97 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 26.64 MPa @Strain 82.74 %, Temperature 23.0 °C | 3864 psi @Strain 82.74 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 26.69 MPa @Strain 88.47 %, Temperature 23.0 °C | 3871 psi @Strain 88.47 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 26.72 MPa @Strain 59.61 %, Temperature 23.0 °C | 3875 psi @Strain 59.61 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 26.74 MPa @Strain 94.29 %, Temperature 23.0 °C | 3878 psi @Strain 94.29 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 26.78 MPa @Strain 100.05 %, Temperature 23.0 °C | 3884 psi @Strain 100.05 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 27.19 MPa @Strain 53.86 %, Temperature 23.0 °C | 3944 psi @Strain 53.86 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 27.2 MPa @Strain 311.55 %, Temperature 60.0 °C | 3950 psi @Strain 311.55 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 27.71 MPa @Strain 48.32 %, Temperature 23.0 °C | 4019 psi @Strain 48.32 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 27.84 MPa @Strain 9.53 %, Temperature 23.0 °C | 4038 psi @Strain 9.53 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 28.18 MPa @Strain 43.08 %, Temperature 23.0 °C | 4087 psi @Strain 43.08 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 28.55 MPa @Strain 71.24 %, Temperature 23.0 °C | 4141 psi @Strain 71.24 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 28.57 MPa @Strain 38.1 %, Temperature 23.0 °C | 4144 psi @Strain 38.1 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 28.66 MPa @Strain 77.01 %, Temperature 23.0 °C | 4157 psi @Strain 77.01 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 28.68 MPa @Strain 65.48 %, Temperature 23.0 °C | 4160 psi @Strain 65.48 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 28.69 MPa @Strain 13.13 %, Temperature 23.0 °C | 4161 psi @Strain 13.13 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 28.72 MPa @Strain 82.75 %, Temperature 23.0 °C | 4165 psi @Strain 82.75 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 28.79 MPa @Strain 88.51 %, Temperature 23.0 °C | 4176 psi @Strain 88.51 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 28.81 MPa @Strain 100.06 %, Temperature 23.0 °C | 4179 psi @Strain 100.06 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 28.83 MPa @Strain 94.28 %, Temperature 23.0 °C | 4181 psi @Strain 94.28 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 28.88 MPa @Strain 33.39 %, Temperature 23.0 °C | 4189 psi @Strain 33.39 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 29.1 MPa @Strain 16.85 %, Temperature 23.0 °C | 4220 psi @Strain 16.85 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 29.1 MPa @Strain 59.73 %, Temperature 23.0 °C | 4220 psi @Strain 59.73 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 29.11 MPa @Strain 28.96 %, Temperature 23.0 °C | 4222 psi @Strain 28.96 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 29.24 MPa @Strain 24.76 %, Temperature 23.0 °C | 4241 psi @Strain 24.76 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 29.26 MPa @Strain 20.72 %, Temperature 23.0 °C | 4244 psi @Strain 20.72 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 29.26 MPa @Strain 2.11 %, Temperature -20.0 °C | 4244 psi @Strain 2.11 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 29.68 MPa @Strain 54.05 %, Temperature 23.0 °C | 4305 psi @Strain 54.05 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 30.2 MPa @Strain 48.58 %, Temperature 23.0 °C | 4380 psi @Strain 48.58 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 30.66 MPa @Strain 43.39 %, Temperature 23.0 °C | 4447 psi @Strain 43.39 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 30.85 MPa @Strain 5.02 %, Temperature 23.0 °C | 4474 psi @Strain 5.02 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 31.04 MPa @Strain 38.4 %, Temperature 23.0 °C | 4502 psi @Strain 38.4 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 31.39 MPa @Strain 33.63 %, Temperature 23.0 °C | 4553 psi @Strain 33.63 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 31.69 MPa @Strain 29.06 %, Temperature 23.0 °C | 4596 psi @Strain 29.06 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 31.95 MPa @Strain 24.68 %, Temperature 23.0 °C | 4634 psi @Strain 24.68 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 32.09 MPa @Strain 8.58 %, Temperature 23.0 °C | 4654 psi @Strain 8.58 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 32.15 MPa @Strain 20.45 %, Temperature 23.0 °C | 4663 psi @Strain 20.45 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 32.28 MPa @Strain 16.35 %, Temperature 23.0 °C | 4682 psi @Strain 16.35 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 32.3 MPa @Strain 12.4 %, Temperature 23.0 °C | 4680 psi @Strain 12.4 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 33.18 MPa @Strain 60.93 %, Temperature 0.000 °C | 4812 psi @Strain 60.93 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 33.49 MPa @Strain 94.46 %, Temperature 0.000 °C | 4857 psi @Strain 94.46 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 33.55 MPa @Strain 66.5 %, Temperature 0.000 °C | 4866 psi @Strain 66.5 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 33.59 MPa @Strain 100.05 %, Temperature 0.000 °C | 4872 psi @Strain 100.05 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 33.59 MPa @Strain 1.94 %, Temperature -40.0 °C | 4872 psi @Strain 1.94 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 33.63 MPa @Strain 88.85 %, Temperature 0.000 °C | 4878 psi @Strain 88.85 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 33.7 MPa @Strain 77.65 %, Temperature 0.000 °C | 4890 psi @Strain 77.65 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 33.76 MPa @Strain 72.07 %, Temperature 0.000 °C | 4896 psi @Strain 72.07 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 33.83 MPa @Strain 83.24 %, Temperature 0.000 °C | 4907 psi @Strain 83.24 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 34.17 MPa @Strain 66.8 %, Temperature 0.000 °C | 4956 psi @Strain 66.8 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 34.23 MPa @Strain 55.21 %, Temperature 0.000 °C | 4965 psi @Strain 55.21 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 34.56 MPa @Strain 1.80 %, Temperature -40.0 °C | 5013 psi @Strain 1.80 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 34.57 MPa @Strain 61.24 %, Temperature 0.000 °C | 5014 psi @Strain 61.24 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 34.58 MPa @Strain 88.95 %, Temperature 0.000 °C | 5015 psi @Strain 88.95 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 34.66 MPa @Strain 100.06 %, Temperature 0.000 °C | 5027 psi @Strain 100.06 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 34.69 MPa @Strain 83.39 %, Temperature 0.000 °C | 5031 psi @Strain 83.39 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 34.74 MPa @Strain 72.3 %, Temperature 0.000 °C | 5039 psi @Strain 72.3 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 34.79 MPa @Strain 94.5 %, Temperature 0.000 °C | 5046 psi @Strain 94.5 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 34.84 MPa @Strain 77.86 %, Temperature 0.000 °C | 5053 psi @Strain 77.86 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 35.63 MPa @Strain 55.55 %, Temperature 0.000 °C | 5168 psi @Strain 55.55 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 35.74 MPa @Strain 3.89 %, Temperature 0.000 °C | 5184 psi @Strain 3.89 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 35.78 MPa @Strain 49.48 %, Temperature 0.000 °C | 5189 psi @Strain 49.48 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 36.48 MPa @Strain 49.95 %, Temperature 0.000 °C | 5291 psi @Strain 49.95 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 36.64 MPa @Strain 4.94 %, Temperature 0.000 °C | 5314 psi @Strain 4.94 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 36.84 MPa @Strain 54.18 %, Temperature -20.0 °C | 5343 psi @Strain 54.18 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 36.9 MPa @Strain 43.91 %, Temperature 0.000 °C | 5350 psi @Strain 43.91 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 37.15 MPa @Strain 59.9 %, Temperature -20.0 °C | 5388 psi @Strain 59.9 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 37.25 MPa @Strain 88.62 %, Temperature -20.0 °C | 5403 psi @Strain 88.62 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 37.34 MPa @Strain 82.86 %, Temperature -20.0 °C | 5416 psi @Strain 82.86 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 37.36 MPa @Strain 71.38 %, Temperature -20.0 °C | 5419 psi @Strain 71.38 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 37.4 MPa @Strain 77.13 %, Temperature -20.0 °C | 5420 psi @Strain 77.13 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 37.41 MPa @Strain 44.46 %, Temperature 0.000 °C | 5426 psi @Strain 44.46 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 37.46 MPa @Strain 65.63 %, Temperature -20.0 °C | 5433 psi @Strain 65.63 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 37.5 MPa @Strain 94.32 %, Temperature -20.0 °C | 5440 psi @Strain 94.32 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 37.65 MPa @Strain 100.06 %, Temperature -20.0 °C | 5461 psi @Strain 100.06 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 37.83 MPa @Strain 38.59 %, Temperature 0.000 °C | 5487 psi @Strain 38.59 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 38.11 MPa @Strain 39.07 %, Temperature 0.000 °C | 5527 psi @Strain 39.07 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 38.44 MPa @Strain 33.5 %, Temperature 0.000 °C | 5575 psi @Strain 33.5 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 38.64 MPa @Strain 48.2 %, Temperature -20.0 °C | 5604 psi @Strain 48.2 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 38.67 MPa @Strain 33.82 %, Temperature 0.000 °C | 5609 psi @Strain 33.82 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 38.93 MPa @Strain 28.64 %, Temperature 0.000 °C | 5646 psi @Strain 28.64 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 39.26 MPa @Strain 8.21 %, Temperature 0.000 °C | 5694 psi @Strain 8.21 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 39.29 MPa @Strain 28.79 %, Temperature 0.000 °C | 5699 psi @Strain 28.79 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 39.42 MPa @Strain 24.07 %, Temperature 0.000 °C | 5717 psi @Strain 24.07 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 39.69 MPa @Strain 19.78 %, Temperature 0.000 °C | 5757 psi @Strain 19.78 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 39.75 MPa @Strain 23.94 %, Temperature 0.000 °C | 5765 psi @Strain 23.94 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 39.89 MPa @Strain 15.68 %, Temperature 0.000 °C | 5786 psi @Strain 15.68 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 39.92 MPa @Strain 11.82 %, Temperature 0.000 °C | 5790 psi @Strain 11.82 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 40.18 MPa @Strain 19.32 %, Temperature 0.000 °C | 5828 psi @Strain 19.32 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 40.35 MPa @Strain 7.09 %, Temperature 0.000 °C | 5852 psi @Strain 7.09 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 40.63 MPa @Strain 14.93 %, Temperature 0.000 °C | 5893 psi @Strain 14.93 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 40.8 MPa @Strain 10.85 %, Temperature 0.000 °C | 5920 psi @Strain 10.85 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 42.54 MPa @Strain 42.05 %, Temperature -20.0 °C | 6170 psi @Strain 42.05 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 43.13 MPa @Strain 29.54 %, Temperature -40.0 °C | 6255 psi @Strain 29.54 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 43.54 MPa @Strain 26.81 %, Temperature -40.0 °C | 6315 psi @Strain 26.81 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 43.62 MPa @Strain 24.92 %, Temperature -40.0 °C | 6327 psi @Strain 24.92 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 44.03 MPa @Strain 22.36 %, Temperature -40.0 °C | 6386 psi @Strain 22.36 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 44.15 MPa @Strain 23.08 %, Temperature -40.0 °C | 6403 psi @Strain 23.08 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 44.17 MPa @Strain 4.87 %, Temperature -20.0 °C | 6406 psi @Strain 4.87 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 44.19 MPa @Strain 21.86 %, Temperature -40.0 °C | 6409 psi @Strain 21.86 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 44.39 MPa @Strain 19.86 %, Temperature -40.0 °C | 6438 psi @Strain 19.86 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 44.48 MPa @Strain 20.94 %, Temperature -40.0 °C | 6451 psi @Strain 20.94 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 44.8 MPa @Strain 36.24 %, Temperature -20.0 °C | 6500 psi @Strain 36.24 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 45.51 MPa @Strain 3.22 %, Temperature -40.0 °C | 6601 psi @Strain 3.22 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 45.73 MPa @Strain 18.98 %, Temperature -40.0 °C | 6633 psi @Strain 18.98 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 46.18 MPa @Strain 30.75 %, Temperature -20.0 °C | 6698 psi @Strain 30.75 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 47.02 MPa @Strain 25.61 %, Temperature -20.0 °C | 6820 psi @Strain 25.61 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 47.34 MPa @Strain 3.08 %, Temperature -40.0 °C | 6866 psi @Strain 3.08 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 47.75 MPa @Strain 20.77 %, Temperature -20.0 °C | 6926 psi @Strain 20.77 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 47.91 MPa @Strain 8.21 %, Temperature -20.0 °C | 6949 psi @Strain 8.21 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 48.26 MPa @Strain 16.26 %, Temperature -20.0 °C | 7000 psi @Strain 16.26 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 48.44 MPa @Strain 12.06 %, Temperature -20.0 °C | 7026 psi @Strain 12.06 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 53.18 MPa @Strain 4.52 %, Temperature -40.0 °C | 7713 psi @Strain 4.52 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 55.25 MPa @Strain 4.42 %, Temperature -40.0 °C | 8013 psi @Strain 4.42 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 56.4 MPa @Strain 20.9 %, Temperature -40.0 °C | 8180 psi @Strain 20.9 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 57.49 MPa @Strain 18.03 %, Temperature -40.0 °C | 8338 psi @Strain 18.03 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 57.69 MPa @Strain 5.84 %, Temperature -40.0 °C | 8367 psi @Strain 5.84 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 59.59 MPa @Strain 16.58 %, Temperature -40.0 °C | 8643 psi @Strain 16.58 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 59.85 MPa @Strain 19.29 %, Temperature -40.0 °C | 8681 psi @Strain 19.29 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 59.85 MPa @Strain 5.83 %, Temperature -40.0 °C | 8681 psi @Strain 5.83 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 59.95 MPa @Strain 7.35 %, Temperature -40.0 °C | 8695 psi @Strain 7.35 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 60.19 MPa @Strain 15.13 %, Temperature -40.0 °C | 8730 psi @Strain 15.13 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 60.57 MPa @Strain 13.6 %, Temperature -40.0 °C | 8785 psi @Strain 13.6 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 60.95 MPa @Strain 8.91 %, Temperature -40.0 °C | 8840 psi @Strain 8.91 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 60.99 MPa @Strain 12.04 %, Temperature -40.0 °C | 8846 psi @Strain 12.04 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 61.22 MPa @Strain 10.5 %, Temperature -40.0 °C | 8879 psi @Strain 10.5 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 61.24 MPa @Strain 17.61 %, Temperature -40.0 °C | 8882 psi @Strain 17.61 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 62.07 MPa @Strain 15.93 %, Temperature -40.0 °C | 9003 psi @Strain 15.93 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 62.14 MPa @Strain 7.35 %, Temperature -40.0 °C | 9013 psi @Strain 7.35 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 62.61 MPa @Strain 14.17 %, Temperature -40.0 °C | 9081 psi @Strain 14.17 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 62.95 MPa @Strain 12.44 %, Temperature -40.0 °C | 9130 psi @Strain 12.44 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 63.0 MPa @Strain 9.00 %, Temperature -40.0 °C | 9140 psi @Strain 9.00 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 63.13 MPa @Strain 10.68 %, Temperature -40.0 °C | 9156 psi @Strain 10.68 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
| Tensile Strength, Yield | 28.0 MPa @Temperature 23.0 °C | 4060 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 30.0 MPa @Temperature 23.0 °C | 4350 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 230 % @Temperature 23.0 °C | 230 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | ||
| 250 % @Temperature 23.0 °C | 250 % @Temperature 73.4 °F | 50%RH; nominal; ISO 527 | |||
| 290 % @Temperature 23.0 °C | 290 % @Temperature 73.4 °F | 50mm/min; 50%RH; ISO 527 | |||
| 300 % @Temperature 23.0 °C | 300 % @Temperature 73.4 °F | 50mm/min; DAM; ISO 527 | |||
| Elongation at Yield | 20 % @Temperature 23.0 °C | 20 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 30 % @Temperature 23.0 °C | 30 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 0.720 GPa @Temperature 23.0 °C | 104 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 1.08 GPa @Temperature 23.0 °C | 157 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Izod Impact, Notched (ISO) | 13.0 kJ/m2 @Temperature -30.0 °C | 6.19 ft-lb/in2 @Temperature -22.0 °F | 50%RH; ISO 180/1A | ||
| 13.0 kJ/m2 @Temperature -30.0 °C | 6.19 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 180/1A | |||
| 27.0 kJ/m2 @Temperature 23.0 °C | 12.8 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| 66.0 kJ/m2 @Temperature 23.0 °C | 31.4 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Charpy Impact, Notched | 1.50 J/cm2 @Temperature -30.0 °C | 7.14 ft-lb/in2 @Temperature -22.0 °F | 50%RH; ISO 179/1eA | ||
| 1.50 J/cm2 @Temperature -30.0 °C | 7.14 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 179/1eA | |||
| 4.00 J/cm2 @Temperature 23.0 °C | 19.0 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| 8.00 J/cm2 @Temperature 23.0 °C | 38.1 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 46.0 °C | 115 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 218 °C | 424 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 240 °C | 464 °F | DAM; Optimum; Extrusion | |||
| 230 - 250 °C | 446 - 482 °F | DAM; Extrusion | |||
| 250 °C | 482 °F | DAM; Optimum; Injection Molding | |||
| 230 - 290 °C | 446 - 554 °F | DAM; Injection Molding | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum; Injection Molding | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM; Injection Molding | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM; Injection Molding | ||
| 80.0 °C | 176 °F | DAM; Extrusion | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM; Injection Molding | ||
| 3.00 - 4.00 hour | 3.00 - 4.00 hour | DAM; Extrusion | |||
| Moisture Content | <= 0.050 % | <= 0.050 % | DAM; Extrusion | ||
| <= 0.050 % | <= 0.050 % | DAM; Injection Molding | |||
| Descriptive Properties | |||||
| Appearance | Black Color | DAM | |||
| Features | Flexibility, Good | DAM | |||
| Flexibility, Good | DAM | ||||
| Toughness, Good | DAM | ||||
| Toughness, Good | DAM | ||||
| Forms | Pellets | DAM | |||
| Generic | Nylon 612 | DAM | |||
| Material Status | Preliminary Data | DAM | |||
| Part Marking Code | >PA612-HI< | ISO 11469; DAM | |||
| Processing Method | Extrusion | DAM | |||
| Product Category | Extrusion Resins | DAM | |||
| Toughened Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA612-HI | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||