- 密度 [g/cm3]: 1.01
- 拉伸強度 [MPa]: 29.0
- 熱變形溫度 [℃]: 83.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in3 | DAM; ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.026 cm/cm @Thickness 2.00 mm | 0.026 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Thickness 2.00 mm | 0.011 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 29.0 MPa @Temperature 23.0 °C | 4210 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 32.0 MPa @Temperature 23.0 °C | 4640 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | ||
| 90 % @Temperature 23.0 °C | 90 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | |||
| 100 % @Temperature 23.0 °C | 100 % @Temperature 73.4 °F | 50mm/min; DAM; ISO 527 | |||
| 230 % @Temperature 23.0 °C | 230 % @Temperature 73.4 °F | 50%RH; nominal; ISO 527 | |||
| 285 % @Temperature 23.0 °C | 285 % @Temperature 73.4 °F | 50mm/min; 50%RH; ISO 527 | |||
| Elongation at Yield | 12 % @Temperature 23.0 °C | 12 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 30 % @Temperature 23.0 °C | 30 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 0.750 GPa @Temperature 23.0 °C | 109 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 1.10 GPa @Temperature 23.0 °C | 160 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Charpy Impact, Notched | 1.20 J/cm2 @Temperature -30.0 °C | 5.71 ft-lb/in2 @Temperature -22.0 °F | 50%RH; ISO 179/1eA | ||
| 1.30 J/cm2 @Temperature -30.0 °C | 6.19 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 179/1eA | |||
| 3.50 J/cm2 @Temperature 23.0 °C | 16.7 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| 8.00 J/cm2 @Temperature 23.0 °C | 38.1 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 83.0 °C | 181 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 216 °C | 421 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 240 - 250 °C | 464 - 482 °F | DAM; Extrusion | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM; Extrusion | ||
| Dry Time | 3.00 hour | 3.00 hour | DAM; Extrusion | ||
| Moisture Content | <= 0.030 % | <= 0.030 % | DAM; Extrusion | ||
| Descriptive Properties | |||||
| Appearance | Black Color | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 612 | DAM | |||
| Material Status | Preliminary Data | DAM | |||
| Part Marking Code | >PA612-HI< | ISO 11469; DAM | |||
| Processing Method | Blow Moldable | DAM | |||
| Extrusion | DAM | ||||
| Product Category | Blow Moldable Resins | DAM | |||
| Extrusion Resins | DAM | ||||
| Toughened Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA612-HI | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||