- 吸水率 [%]: 0.15
- 缺口沖擊強度: 1.0
- 拉伸強度 [MPa]: 169.0
- 彎曲模量 [MPa]: 14.5
- 熱變形溫度 [℃]: 212.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 | ||
| Water Absorption | 0.15 % | 0.15 % | @ 24 hrs; ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0080 cm/cm | 0.0020 - 0.0080 in/in | ASTM D955 | ||
| Linear Mold Shrinkage, Transverse | 0.010 - 0.020 cm/cm | 0.010 - 0.020 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 169 MPa | 24500 psi | Type I, 5.1 mm/min; ASTM D638 | ||
| Tensile Strength, Yield | 169 MPa | 24500 psi | ASTM D638 | ||
| Elongation at Break | 2.9 % | 2.9 % | Type I, 5.1 mm/min; ASTM D638 | ||
| Tensile Modulus | 19.3 GPa | 2800 ksi | Type I, 5.1 mm/min; ASTM D638 | ||
| Flexural Strength | 269 MPa | 39000 psi | ASTM D790 | ||
| Flexural Modulus | 14.5 GPa | 2100 ksi | ASTM D790 | ||
| Izod Impact, Notched | 1.00 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 1.87 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Injection Molded; ASTM D256A | ||
| Coefficient of Friction, Dynamic | 0.14 | 0.14 | vs. Steel - Dynamic; ASTM D1894 | ||
| Coefficient of Friction, Static | 0.26 | 0.26 | vs. Steel - Static; ASTM D1894 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 100 - 1000 ohm-cm | 100 - 1000 ohm-cm | ASTM D257 | ||
| Surface Resistance | 100 - 1000 ohm | 100 - 1000 ohm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C @Thickness 3.18 mm | 414 °F @Thickness 0.125 in | Unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C @Thickness 3.18 mm | 388 °F @Thickness 0.125 in | Unannealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 243 - 271 °C | 469 - 520 °F | |||
| Mold Temperature | 82.2 - 93.3 °C | 180 - 200 °F | |||
| Drying Temperature | 71.1 - 82.2 °C | 160 - 180 °F | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |||
| Descriptive Properties | |||||
| Appearance | Black | ||||
| Features | Electrically Conductive | ||||
| Good Wear Resistance | |||||
| High Stiffness | |||||
| Lubricated | |||||
| Forms | Pellets | ||||
| Generic Material | Nylon 612 | ||||
| Generic Name | Polyamide 612 (Nylon 612) | ||||
| Processing Method | Injection Molding | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| RoHS Compliance | RoHS Compliant | ||||
| Uses | Appliance Components | ||||
| Automotive Applications | |||||
| Bearings | |||||
| Business Equipment | |||||
| Consumer Applications | |||||
| Conveyor Parts | |||||
| Gears | |||||
| Industrial Applications | |||||
| Printer Parts | |||||
| Pulleys | |||||
| Rollers | |||||