- 熔體流動速率 [g/10min]: 1.5
- 密度 [g/cm3]: 1.05
- 拉伸強度 [MPa]: 16.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in3 | |
| Moisture Absorption at Equilibrium | 0.70 % | 0.70 % | Humidity Absorption |
| Melt Flow | 1.5 g/10 min @Load 2.16 kg, Temperature 235 °C | 1.5 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 16.0 MPa @Strain 50.0 % | 2320 psi @Strain 50.0 % | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Tensile Modulus | 0.165 GPa | 23.9 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB | NB | Low Temp | |
| Charpy Impact, Notched | NB | NB | |
| 0.440 J/cm2 @Temperature -30.0 °C | 2.09 ft-lb/in2 @Temperature -22.0 °F | ||
| Thermal Properties | Metric | English | Comments |
| Melting Point | 170 °C | 338 °F | 10°C/min |
| Deflection Temperature at 1.8 MPa (264 psi) | 36.0 °C | 96.8 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.10 mm | HB @Thickness 0.122 in | ||