- 熔體流動速率 [g/10min]: 12.0
- 密度 [g/cm3]: 1.06
- 吸水率 [%]: 0.3
- 缺口沖擊強度: 0.534
- 拉伸強度 [MPa]: 81.4
- 彎曲模量 [MPa]: 2.03
- 硬度: 85.0
- 熱變形溫度 [℃]: 154.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in3 | ASTM D792 |
| Water Absorption | 0.30 % @Time 86400 sec | 0.30 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.011 cm/cm @Thickness 3.17 mm | 0.011 in/in @Thickness 0.125 in | ASTM D955 |
| Melt Flow | 12 g/10 min @Load 3.80 kg, Temperature 230 °C | 12 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 85 | 85 | ASTM D785 |
| Tensile Strength, Yield | 81.4 MPa | 11800 psi | ASTM D638 |
| Elongation at Yield | 10 % | 10 % | ASTM D638 |
| Flexural Strength | 98.6 MPa | 14300 psi | ASTM D790 |
| Flexural Modulus | 2.03 GPa | 295 ksi | ASTM D790 |
| Poissons Ratio | 0.40 | 0.40 | ASTM E132 |
| Izod Impact, Notched | 0.534 J/cm @Thickness 3.17 mm | 1.00 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 72.0 μm/m-°C | 40.0 μin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 310 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | Unannealed; ASTM D648 |
| Vicat Softening Point | 108 °C | 226 °F | Rate B (120°C/h); ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 0.70 % | 0.70 % | ASTM D1003 |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |
| IR Transmittance | 89 - 90 % | 89 - 90 % | ASTM D1003 |