- 密度 [g/cm3]: 1.11
- 缺口沖擊強度: 14.0
- 彎曲模量 [MPa]: 7.90
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in3 | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 130 MPa | 18900 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.0 - 4.0 % | 2.0 - 4.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 10.3 GPa | 1490 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 171 MPa | 24800 psi | break, 2 mm/min; ISO 178 |
| Flexural Modulus | 7.90 GPa | 1150 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m2 | 6.66 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m2 | 23.8 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D257 |