- 密度 [g/cm3]: 1.27
- 缺口沖擊強度: 1.17
- 彎曲模量 [MPa]: 13.85
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in3 | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 124 MPa | 18000 psi | ASTM D638 |
| Elongation at Break | 2.7 % | 2.7 % | ASTM D638 |
| Tensile Modulus | 15.72 GPa | 2280 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 206 MPa | 29900 psi | ASTM D790 |
| Flexural Modulus | 13.85 GPa | 2009 ksi | ASTM D790 |
| Izod Impact, Notched | 1.17 J/cm | 2.19 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.94 J/cm | 13.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 168 °C @Thickness 3.20 mm | 334 °F @Thickness 0.126 in | unannealed; ASTM D648 |