- 密度 [g/cm3]: 11.0
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 3.47
- 拉伸強度 [MPa]: 35.2
- 彎曲模量 [MPa]: 6.89
- 硬度: 120.0
- 熱變形溫度 [℃]: 121.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 11.0 g/cc | 0.397 lb/in3 | ASTM D792 |
| Water Absorption | 0.10 % @Time 86400 sec | 0.10 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 3.17 mm | 0.0020 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 35.2 MPa | 5100 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 48.3 MPa | 7000 psi | ASTM D790 |
| Flexural Modulus | 6.89 GPa | 1000 ksi | ASTM D790 |
| Izod Impact, Notched | 3.47 J/cm @Thickness 3.17 mm | 6.50 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.0 - 100 ohm-cm | 1.0 - 100 ohm-cm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 16.2 μm/m-°C | 9.00 μin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 121 °C | 250 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | Unannealed; ASTM D648 |