- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 0.14
- 缺口沖擊強(qiáng)度: 15.0
- 拉伸強(qiáng)度 [MPa]: 100.0
- 斷裂伸長率 [%]: 147
- 彎曲模量 [MPa]: 5.90
- 熱變形溫度 [℃]: 175.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in3 | ISO 1183 |
| Water Absorption | 0.14 % @Time 86400 sec | 0.14 % @Time 24.0 hour | ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 100 MPa | 14500 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 4.5 % | 4.5 % | 5 mm/min; ISO 527 |
| Flexural Yield Strength | 147 MPa | 21300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 5.90 GPa | 856 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m2 | 7.14 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 65.0 kJ/m2 | 30.9 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 22.0 μm/m-°C @Temperature 23.0 - 60.0 °C | 12.2 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 117 μm/m-°C @Temperature 23.0 - 60.0 °C | 65.0 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |