- 密度 [g/cm3]: 1.37
- 缺口沖擊強度: 2.56
- 彎曲模量 [MPa]: 7.58
- 熱變形溫度 [℃]: 176.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in3 | ASTM D792 |
| 1.37 g/cc | 0.0495 lb/in3 | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0018 cm/cm @Time 86400 sec | 0.0018 in/in @Time 24.0 hour | ISO 294 |
| 0.0020 cm/cm @Time 86400 sec | 0.0020 in/in @Time 24.0 hour | ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Time 86400 sec | 0.0070 in/in @Time 24.0 hour | ASTM D955 |
| 0.0073 cm/cm @Time 86400 sec | 0.0073 in/in @Time 24.0 hour | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 135 MPa | 19600 psi | ASTM D638 |
| 152 MPa | 22000 psi | ISO 527 | |
| Elongation at Break | 9.0 % | 9.0 % | ISO 527 |
| 10.5 % | 10.5 % | ASTM D638 | |
| Tensile Modulus | 8.27 GPa | 1200 ksi | 50 mm/min; ASTM D638 |
| 8.76 GPa | 1270 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| 213 MPa | 30900 psi | ISO 178 | |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 |
| 9.00 GPa | 1310 ksi | ISO 178 | |
| Izod Impact, Notched | 2.56 J/cm | 4.80 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 14.41 J/cm | 27.00 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m2 | 8.57 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 75.0 kJ/m2 | 35.7 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 176 °C @Thickness 3.20 mm | 349 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 166 °C | 331 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 170 °C @Thickness 3.20 mm | 338 °F @Thickness 0.126 in | unannealed; ASTM D648 | |