- 密度 [g/cm3]: 1.24
- 缺口沖擊強度: 1.49
- 彎曲模量 [MPa]: 5.86
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in3 | ISO 1183 |
| 1.243 g/cc | 0.04491 lb/in3 | ASTM D792 | |
| Moisture Absorption | 0.140 % | 0.140 % | 50% RH, 24 hrs; ASTM D570 |
| 0.220 % | 0.220 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm @Time 86400 sec | 0.0020 - 0.0030 in/in @Time 24.0 hour | ASTM D955 |
| 0.0021 - 0.0030 cm/cm @Time 86400 sec | 0.0021 - 0.0030 in/in @Time 24.0 hour | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0080 cm/cm @Time 86400 sec | 0.0070 - 0.0080 in/in @Time 24.0 hour | ASTM D955 |
| 0.0074 - 0.0081 cm/cm @Time 86400 sec | 0.0074 - 0.0081 in/in @Time 24.0 hour | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 106 MPa | 15400 psi | ASTM D638 |
| 108 MPa | 15700 psi | ISO 527 | |
| Elongation at Break | 4.6 % | 4.6 % | ISO 527 |
| 4.7 % | 4.7 % | ASTM D638 | |
| Tensile Modulus | 6.55 GPa | 950 ksi | 50 mm/min; ASTM D638 |
| 6.58 GPa | 954 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 169 MPa | 24500 psi | ISO 178 |
| 170 MPa | 24700 psi | ASTM D790 | |
| Flexural Modulus | 5.86 GPa | 850 ksi | ASTM D790 |
| 6.24 GPa | 905 ksi | ISO 178 | |
| Izod Impact, Notched | 1.49 J/cm | 2.79 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.50 J/cm | 17.8 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m2 | 7.14 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 58.0 kJ/m2 | 27.6 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J | 9.59 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 43.7 μm/m-°C @Temperature -40.0 - 40.0 °C | 24.3 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 43.7 μm/m-°C @Temperature -40.0 - 40.0 °C | 24.3 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 112 μm/m-°C @Temperature -40.0 - 40.0 °C | 62.2 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 113 μm/m-°C @Temperature -40.0 - 40.0 °C | 62.8 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 162 °C | 324 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 163 °C @Thickness 3.20 mm | 325 °F @Thickness 0.126 in | unannealed; ASTM D648 | |