- 密度 [g/cm3]: 1.48
- 缺口沖擊強(qiáng)度: 0.97
- 拉伸強(qiáng)度 [MPa]: 113.0
- 斷裂伸長率 [%]: 148
- 彎曲模量 [MPa]: 0.0100
- 熱變形溫度 [℃]: 176.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in3 | ASTM D 792 |
| 1.48 g/cc | 0.0535 lb/in3 | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec | 0.0020 - 0.0040 in/in @Time 24.0 hour | ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Time 86400 sec | 0.0080 - 0.010 in/in @Time 24.0 hour | ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 113 MPa | 16400 psi | 5 mm/min; ISO 527 |
| 121 MPa | 17500 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 113 MPa | 16400 psi | 5 mm/min; ISO 527 |
| 121 MPa | 17500 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 12.28 GPa | 1781 ksi | 1 mm/min; ISO 527 |
| 12.8 GPa | 1860 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 143 MPa | 20700 psi | brk, 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Yield Strength | 148 MPa | 21500 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 0.0100 GPa | 1.45 ksi | 2 mm/min; ISO 178 |
| 8.93 GPa | 1300 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.970 J/cm @Temperature 23.0 °C | 1.82 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 5.77 J/cm @Temperature 23.0 °C | 10.8 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Izod Impact, Notched (ISO) | 1.00 kJ/m2 @Temperature 23.0 °C | 0.476 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m2 @Temperature 23.0 °C | 14.3 ft-lb/in2 @Temperature 73.4 °F | 80*10*4; ISO 180/1U |
| Impact Test | 16.0 J | 11.8 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 176 °C @Thickness 3.20 mm | 349 °F @Thickness 0.126 in | unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 176 °C | 349 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 166 °C @Thickness 3.20 mm | 331 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |