- 缺口沖擊強度: 1.3
- 彎曲模量 [MPa]: 8.07
- 熱變形溫度 [℃]: 175.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | ASTM D792 | ||
| Linear Mold Shrinkage, Flow | 0.00050 - 0.0020 cm/cm | 0.00050 - 0.0020 in/in | ASTM D955 | ||
| Linear Mold Shrinkage, Transverse | 0.00050 - 0.0020 cm/cm | 0.00050 - 0.0020 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 119 MPa | 17300 psi | ASTM D638 | ||
| Elongation at Break | 5.2 % | 5.2 % | Type I, 5.1 mm/min; ASTM D638 | ||
| Tensile Modulus | 8.00 GPa | 1160 ksi | Type I, 5.1 mm/min; ASTM D638 | ||
| Flexural Strength | 192 MPa | 27800 psi | ASTM D790 | ||
| Flexural Modulus | 8.07 GPa | 1170 ksi | ASTM D790 | ||
| Izod Impact, Notched | 1.30 J/cm @Thickness 3.18 mm, Temperature 23.0 °C | 2.44 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Injection Molded; ASTM D256A | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1000 - 100000 ohm-cm | 1000 - 100000 ohm-cm | ASTM D257 | ||
| Surface Resistance | 1000 - 100000 ohm | 1000 - 100000 ohm | ASTM D257 | ||
| Static Decay | 0.0020 sec | 0.0020 sec | (Mil-B-81705C), 12% RH, 5000 kV to 50 kV | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C @Thickness 6.35 mm | 347 °F @Thickness 0.250 in | Unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 163 °C @Thickness 6.35 mm | 325 °F @Thickness 0.250 in | Unannealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 254 - 277 °C | 489 - 531 °F | |||
| Descriptive Properties | |||||
| Features | Good Chemical Resistance | ||||
| Good Stability | |||||
| Low to No Water Absorption | |||||
| Filler / Reinforcement | Carbon Fiber Reinforcement, 20% Filler by Weight | ||||
| Forms | Pellets | ||||
| Generic Material | Nylon 12 | ||||
| Generic Name | Polyamide 12 (Nylon 12) | ||||
| Processing Method | Injection Molding | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| RoHS Compliance | RoHS Compliant | ||||
| Uses | Aerospace Applications | ||||
| Automotive Electronics | |||||
| Business Equipment | |||||
| Computer Components | |||||
| Connectors | |||||
| Consumer Applications | |||||
| Electrical Housing | |||||
| Electrical/Electronic Applications | |||||
| Housings | |||||
| Marine Applications | |||||
| Sporting Goods | |||||