- 吸水率 [%]: 0.1
- 缺口沖擊強度: 0.267
- 彎曲模量 [MPa]: 13.8
- 熱變形溫度 [℃]: 193.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.65 g/cc | 1.65 g/cc | ASTM D792 |
| Water Absorption | 0.10 % @Thickness 3.17 mm | 0.10 % @Thickness 0.125 in | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0030 cm/cm | 0.0020 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Elongation at Break | 0.60 % | 0.60 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 19.3 GPa | 2800 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 99.3 MPa | 14400 psi | ASTM D790 |
| Flexural Modulus | 13.8 GPa | 2000 ksi | ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 0.500 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Method A, Injection Molded; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 - 1.00e+16 ohm-cm | 1.00e+15 - 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 1.00e+13 - 1.00e+14 ohm | 1.00e+13 - 1.00e+14 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 2.00 - 3.00 W/m-K | 13.9 - 20.8 BTU-in/hr-ft2-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 193 °C | 380 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 - 277 °C | 500 - 530 °F | Molding |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |