- 缺口沖擊強度: 0.8
- 拉伸強度 [MPa]: 44.8
- 彎曲模量 [MPa]: 8.27
- 熱變形溫度 [℃]: 155.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 11.0 g/cc | 11.0 g/cc | ASTM D792 | ||
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 44.8 MPa | 6500 psi | Type I, 5.1 mm/min; ASTM D638 | ||
| Elongation at Break | 1.0 % | 1.0 % | Type I, 5.1 mm/min; ASTM D638 | ||
| Tensile Modulus | 8.96 GPa | 1300 ksi | Type I, 5.1 mm/min; ASTM D638 | ||
| Flexural Strength | 68.9 MPa | 9990 psi | ASTM D790 | ||
| Flexural Modulus | 8.27 GPa | 1200 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.800 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 1.50 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Injection Molded; ASTM D256A | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C @Thickness 6.35 mm | 311 °F @Thickness 0.250 in | Unannealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 - 288 °C | 500 - 550 °F | |||
| Mold Temperature | 82.2 - 149 °C | 180 - 300 °F | |||
| Drying Temperature | 79.4 °C | 175 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Descriptive Properties | |||||
| Features | High Density | ||||
| Non-Toxic | |||||
| Forms | Pellets | ||||
| Generic Material | Nylon 12 | ||||
| Generic Name | Polyamide 12 (Nylon 12) | ||||
| Processing Method | Injection Molding | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Uses | Industrial Applications | ||||
| Medical/Healthcare Applications | |||||
| Projectiles | |||||
| Radiation Shielding | |||||
| Sporting Goods | |||||
| Weighting & Balancing | |||||