- 密度 [g/cm3]: 1.084
- 吸水率 [%]: 0.35
- 缺口沖擊強度: 1.07
- 斷裂伸長率 [%]: 93.0
- 彎曲強度 [MPa]: 66.0
- 彎曲模量 [MPa]: 4.50
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.084 g/cc | 0.03916 lb/in3 | ASTM D792 |
| Water Absorption | 0.35 % | 0.35 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0070 cm/cm @Thickness 3.17 mm | 0.0070 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ASTM D638 |
| Elongation at Break | 1.0 - 3.0 % | 1.0 - 3.0 % | ASTM D638 |
| Tensile Modulus | 4.50 GPa | 653 ksi | ASTM D638 |
| Flexural Yield Strength | 93.0 MPa | 13500 psi | ASTM D790 |
| Flexural Modulus | 4.50 GPa | 653 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 6.35 mm | 2.00 ft-lb/in @Thickness 0.250 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 154 °C | 309 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 238 - 271 °C | 460 - 520 °F | Stock |
| Mold Temperature | 93.0 °C | 199 °F | |
| Drying Temperature | 93.0 °C | 199 °F | |