- 缺口沖擊強度: 1.12
- 拉伸強度 [MPa]: 44.8
- 彎曲模量 [MPa]: 4.96
- 熱變形溫度 [℃]: 159.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 6.88 g/cc | 6.88 g/cc | ASTM D792 | ||
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0060 cm/cm | 0.0050 - 0.0060 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 44.8 MPa | 6500 psi | Type I, 5.1 mm/min; ASTM D638 | ||
| Elongation at Break | 1.8 % | 1.8 % | Type I, 5.1 mm/min; ASTM D638 | ||
| Tensile Modulus | 7.58 GPa | 1100 ksi | Type I, 5.1 mm/min; ASTM D638 | ||
| Flexural Modulus | 4.96 GPa | 719 ksi | ASTM D790 | ||
| Izod Impact, Notched | 1.12 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 2.10 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Injection Molded; ASTM D256A | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 159 °C @Thickness 6.35 mm | 318 °F @Thickness 0.250 in | Unannealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 - 288 °C | 500 - 550 °F | |||
| Mold Temperature | 82.2 - 149 °C | 180 - 300 °F | |||
| Drying Temperature | 79.4 °C @Time 14400 sec | 175 °F @Time 4.00 hour | |||
| Descriptive Properties | |||||
| Features | Non-Toxic | ||||
| Forms | Pellets | ||||
| Generic Name | Polyamide 12 (Nylon 12) | ||||
| Processing Method | Injection Molding | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Uses | Industrial Applications | ||||
| Medical/Healthcare Applications | |||||
| Projectiles | |||||
| Radiation Shielding | |||||
| Sporting Goods | |||||
| Weighting & Balancing | |||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.