- 密度 [g/cm3]: 1.03
- 吸水率 [%]: 1.0
- 拉伸強度 [MPa]: 60.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in3 | |
| Water Absorption | 1.0 % | 1.0 % | |
| Moisture Absorption at Equilibrium | <= 0.50 % | <= 0.50 % | Humidity Absorption |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | |
| Elongation at Break | 9.0 % | 9.0 % | |
| Elongation at Yield | 7.0 % | 7.0 % | |
| Modulus of Elasticity | 2.10 GPa | 305 ksi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 3.00e+14 ohm-cm | 3.00e+14 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 3.0 @Frequency 100 Hz | 3.0 @Frequency 100 Hz | |
| Dissipation Factor | 0.038 @Frequency 100 Hz | 0.038 @Frequency 100 Hz | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | <= 50.0 μm/m-°C @Temperature 20.0 °C | <= 27.8 μin/in-°F @Temperature 68.0 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | |
| Vicat Softening Point | 190 °C | 374 °F | 50°C/hr/50 N |