- 缺口沖擊強度: 1.1
- 拉伸強度 [MPa]: 27.2
- 彎曲模量 [MPa]: 4.96
- 熱變形溫度 [℃]: 138.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 11.0 g/cc | 11.0 g/cc | ASTM D792 | ||
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 27.2 MPa | 3950 psi | Type I, 5.1 mm/min; ASTM D638 | ||
| Elongation at Break | 1.8 % | 1.8 % | Type I, 5.1 mm/min; ASTM D638 | ||
| Tensile Modulus | 8.27 GPa | 1200 ksi | Type I, 5.1 mm/min; ASTM D638 | ||
| Flexural Strength | 48.3 MPa | 7010 psi | ASTM D790 | ||
| Flexural Modulus | 4.96 GPa | 719 ksi | ASTM D790 | ||
| Poissons Ratio | 0.35 | 0.35 | ASTM E132 | ||
| Shear Modulus | 3.06 GPa | 444 ksi | Calculated | ||
| Izod Impact, Notched | 1.10 J/cm @Thickness 3.18 mm, Temperature 23.0 °C | 2.06 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Injection Molded; ASTM D256A | ||
| Izod Impact, Unnotched | 3.70 J/cm @Thickness 3.18 mm, Temperature 23.0 °C | 6.93 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Injection Molded; ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 63.0 μm/m-°C @Temperature 0.000 - 32.0 °C | 35.0 μin/in-°F @Temperature 32.0 - 89.6 °F | ASTM E831 | ||
| 100 μm/m-°C @Temperature 60.0 - 100 °C | 55.6 μin/in-°F @Temperature 140 - 212 °F | ASTM E831 | |||
| CTE, linear, Transverse to Flow | 57.0 μm/m-°C @Temperature 0.000 - 32.0 °C | 31.7 μin/in-°F @Temperature 32.0 - 89.6 °F | ASTM E831 | ||
| 84.0 μm/m-°C @Temperature 60.0 - 100 °C | 46.7 μin/in-°F @Temperature 140 - 212 °F | ASTM E831 | |||
| Thermal Conductivity | 3.50 W/m-K | 24.3 BTU-in/hr-ft2-°F | The value listed as thermal conductivity, ASTM C177, was tested in accordance with ASTM E1461.; ASTM C177 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 138 °C @Thickness 6.35 mm | 280 °F @Thickness 0.250 in | Unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 87.8 °C @Thickness 6.35 mm | 190 °F @Thickness 0.250 in | Unannealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 - 288 °C | 500 - 550 °F | |||
| Mold Temperature | 82.2 - 149 °C | 180 - 300 °F | |||
| Drying Temperature | 79.4 °C | 175 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Descriptive Properties | |||||
| Additive | Impact Modifier | ||||
| Appearance | Natural Color | ||||
| Features | High Density | ||||
| Impact Modified | |||||
| Non-Toxic | |||||
| Forms | Pellets | ||||
| Generic Material | Nylon 12 | ||||
| Generic Name | Polyamide 12 (Nylon 12) | ||||
| Processing Method | Injection Molding | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Uses | Industrial Applications | ||||
| Medical/Healthcare Applications | |||||
| Projectiles | |||||
| Radiation Shielding | |||||
| Sporting Goods | |||||
| Weighting & Balancing | |||||