- 密度 [g/cm3]: 1.03
- 吸水率 [%]: 0.12
- 缺口沖擊強度: 1.61
- 彎曲模量 [MPa]: 1.64
- 硬度: 108.0
- 熱變形溫度 [℃]: 175.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in3 | ASTM D792 |
| Water Absorption | 0.12 % | 0.12 % | 24 hrs; ASTM D570 |
| Water Absorption at Saturation | 0.66 % | 0.66 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 108 | 108 | ASTM D785 |
| Hardness, Shore D | 76 | 76 | ASTM D2240 |
| Tensile Strength | 54.5 MPa | 7900 psi | ASTM D638 |
| Elongation at Break | >= 50 % | >= 50 % | ASTM D638 |
| Tensile Modulus | 1.59 GPa | 230 ksi | ASTM D638 |
| Flexural Strength | 62.1 MPa | 9000 psi | ASTM D790 |
| Flexural Modulus | 1.64 GPa | 238 ksi | ASTM D790 |
| Compressive Strength | 68.9 MPa | 10000 psi | ASTM D695 |
| Compressive Modulus | 1.54 GPa | 224 ksi | ASTM D695 |
| Shear Strength | 42.1 MPa | 6100 psi | ASTM D732 |
| Izod Impact, Notched | 1.61 J/cm | 3.02 ft-lb/in | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.2 - 0.3 | 0.2 - 0.3 | ASTM D1894 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.7 @Frequency 60.0 Hz | 3.7 @Frequency 60.0 Hz | ASTM D150 |
| 3.7 @Frequency 1000 Hz | 3.7 @Frequency 1000 Hz | ASTM D150 | |
| 3.7 @Frequency 1.00e+6 Hz | 3.7 @Frequency 1.00e+6 Hz | ASTM D150 | |
| Dielectric Strength | 19.7 - 23.6 kV/mm | 500 - 600 kV/in | ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 99.0 μm/m-°C | 55.0 μin/in-°F | ASTM D696 |
| Melting Point | 177 °C | 351 °F | ASTM D789 |
| Maximum Service Temperature, Air | 121 °C | 250 °F | Continuous |
| 149 °C | 300 °F | Intermittent | |
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 51.1 °C | 124 °F | ASTM D648 |
- 關(guān)鍵詞:
- 供應(yīng)
- PA12
- Cast Nylons Nycast? 12 Cast Nylon 12