- 密度 [g/cm3]: 1.02
- 吸水率 [%]: 0.9
- 拉伸強(qiáng)度 [MPa]: 38.0
- 彎曲模量 [MPa]: 1.20
- 熱變形溫度 [℃]: 130.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in3 | ISO 1183 |
| Water Absorption | 0.90 % @Temperature 23.0 °C, Time 86400 sec | 0.90 % @Temperature 73.4 °F, Time 24.0 hour | ISO 62 |
| Moisture Absorption at Equilibrium | 0.70 % @Temperature 20.0 °C | 0.70 % @Temperature 68.0 °F | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm @Thickness 2.00 mm, Time 86400 sec | 0.0080 in/in @Thickness 0.0787 in, Time 24.0 hour | |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Thickness 2.00 mm, Time 86400 sec | 0.0080 in/in @Thickness 0.0787 in, Time 24.0 hour | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 72 | 72 | After 15 sec, Conditioned 15 days at 23°C - 50% RH; ISO 868 |
| Tensile Strength at Break | 64.0 MPa | 9280 psi | Conditioned 15 days at 23°C - 50% RH; ISO 527 |
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | Conditioned 15 days at 23°C - 50% RH; ISO 527 |
| Elongation at Break | <= 250 % | <= 250 % | Conditioned 15 days at 23°C - 50% RH; ISO 527 |
| Elongation at Yield | 7.0 % | 7.0 % | Conditioned 15 days at 23°C - 50% RH; ISO 527 |
| Tensile Modulus | 1.17 GPa | 170 ksi | Conditioned 15 days at 23°C - 50% RH; ISO 527 |
| Flexural Modulus | 1.20 GPa | 174 ksi | Conditioned 15 days at 23°C - 50% RH; ISO 178 |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179 |
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179 | |
| Charpy Impact, Notched | 0.500 J/cm2 @Temperature -30.0 °C | 2.38 ft-lb/in2 @Temperature -22.0 °F | ISO 179 |
| 0.900 J/cm2 @Temperature 23.0 °C | 4.28 ft-lb/in2 @Temperature 73.4 °F | ISO 179 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 180 °C | 356 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75 |
| Processing Properties | Metric | English | Comments |
| Nozzle Temperature | 250 °C | 482 °F | Recommended |
| 230 - 280 °C | 446 - 536 °F | ||
| Mold Temperature | 40.0 °C | 104 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |