- 密度 [g/cm3]: 1.01
- 吸水率 [%]: 0.9
- 拉伸強度 [MPa]: 43.0
- 彎曲模量 [MPa]: 1.18
- 熱變形溫度 [℃]: 130.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.90 % @Temperature 23.0 °C, Time 86400 sec | 0.90 % @Temperature 73.4 °F, Time 24.0 hour | ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.70 % @Temperature 20.0 °C | 0.70 % @Temperature 68.0 °F | 50% RH; ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 69 | 69 | After 15 sec, Conditioned 15 days at 23°C - 50% RH; ISO 868 | ||
| 75 | 75 | Instantaneous, Conditioned 15 days at 23°C - 50% RH; ISO 868 | |||
| Tensile Strength at Break | 50.0 MPa | 7250 psi | Conditioned 15 days at 23°C - 50% RH; ISO 527 | ||
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | Conditioned 15 days at 23°C - 50% RH; ISO 527 | ||
| Elongation at Break | <= 200 % | <= 200 % | Conditioned 15 days at 23°C - 50% RH; ISO 527 | ||
| Elongation at Yield | 5.0 % | 5.0 % | Conditioned 15 days at 23°C - 50% RH; ISO 527 | ||
| Tensile Modulus | 1.44 GPa | 209 ksi | Conditioned 15 days at 23°C - 50% RH; ISO 527 | ||
| Flexural Modulus | 1.18 GPa | 171 ksi | Conditioned 15 days at 23°C - 50% RH; ISO 178 | ||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179 | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179 | |||
| Charpy Impact, Notched | 0.600 J/cm2 @Temperature -30.0 °C | 2.86 ft-lb/in2 @Temperature -22.0 °F | ISO 179 | ||
| 1.10 J/cm2 @Temperature 23.0 °C | 5.23 ft-lb/in2 @Temperature 73.4 °F | ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 180 °C | 356 °F | ISO 11357 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 230 - 270 °C | 446 - 518 °F | Extrusion Temperature Range | ||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |||
| Descriptive Properties | |||||
| Extrusion Temperature | 240°C | Recommended | |||