- 吸水率 [%]: 3.0
- 拉伸強度 [MPa]: 66.0
- 熱變形溫度 [℃]: 135.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.00 g/cc | 1.00 g/cc | ISO 1183 | ||
| Water Absorption | 3.0 % | 3.0 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 83 | 83 | ISO 868 | ||
| Ball Indentation Hardness | 90.0 MPa | 13100 psi | ISO 2039 | ||
| Tensile Strength at Break | 45.0 MPa | 6530 psi | ISO 527 | ||
| Tensile Strength, Yield | 66.0 MPa | 9570 psi | ISO 527 | ||
| Elongation at Break | >= 50 % | >= 50 % | ISO 527 | ||
| Elongation at Yield | 6.0 % | 6.0 % | ISO 527 | ||
| Modulus of Elasticity | 1.47 GPa | 213 ksi | ISO 527 | ||
| Charpy Impact, Notched | 1.30 J/cm2 | 6.19 ft-lb/in2 | ISO 179 | ||
| NB | NB | ISO 179 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+11 ohm-cm | >= 1.00e+11 ohm-cm | IEC 60093 | ||
| Surface Resistivity per Square | >= 1.00e+13 ohm | >= 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | IEC 60243-1 | ||
| Comparative Tracking Index | 60 V | 60 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 90.0 μm/m-°C | 50.0 μin/in-°F | ISO 11359 | ||
| Melting Point | 155 °C | 311 °F | DIN EN ISO 314 | ||
| Maximum Service Temperature, Air | 100 °C | 212 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | ISO 75 | ||
| Glass Transition Temp, Tg | 155 °C | 311 °F | DIN EN ISO 3146 | ||
| Flammability, UL94 | HB | HB | |||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 90 % | 90 % | Transparent, thickness not specified | ||
| Descriptive Properties | |||||
| Bondability | yes | ||||
| Color | transparent | ||||
| Physiological indifference according | Yes | FDA, NSF | |||
| yes | EEC | ||||
| UV stabilization | yes | ||||