- 熔體流動(dòng)速率 [g/10min]: 50.0
- 密度 [g/cm3]: 1.02
- 吸水率 [%]: 1.6
- 拉伸強(qiáng)度 [MPa]: 46.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in3 | |
| Water Absorption | 1.6 % | 1.6 % | |
| Melt Flow | 50 g/10 min @Load 2.16 kg, Temperature 235 °C | 50 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 9.0 % | 9.0 % | 50 mm/min |
| Tensile Modulus | 1.50 GPa | 218 ksi | 1 mm/min |
| Electrical Properties | Metric | English | Comments |
| Dissipation Factor | 0.000298 @Frequency 100 Hz | 0.000298 @Frequency 100 Hz | |
| 0.000326 @Frequency 1e+6 Hz | 0.000326 @Frequency 1e+6 Hz | ||
| Thermal Properties | Metric | English | Comments |
| Melting Point | 174 °C | 345 °F | 10°C/min |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| V-2 @Thickness 3.20 mm | V-2 @Thickness 0.126 in | ||