- 熔體流動速率 [g/10min]: 3.0
- 密度 [g/cm3]: 1.15
- 彎曲強(qiáng)度 [MPa]: 161.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in3 | |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 235 °C | 3.0 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 161 MPa | 23400 psi | 5 mm/min |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min |
| Tensile Modulus | 15.0 GPa | 2180 ksi | 1 mm/min |
| Charpy Impact Unnotched | 6.12 J/cm2 | 29.1 ft-lb/in2 | |
| 5.91 J/cm2 @Temperature -30.0 °C | 28.1 ft-lb/in2 @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 1.45 J/cm2 | 6.90 ft-lb/in2 | |
| 0.940 J/cm2 @Temperature -30.0 °C | 4.47 ft-lb/in2 @Temperature -22.0 °F | ||
| Thermal Properties | Metric | English | Comments |
| Melting Point | 174 °C | 345 °F | 10°C/min |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.10 mm | HB @Thickness 0.122 in | ||