- 熔體流動速率 [g/10min]: 42.0
- 密度 [g/cm3]: 1.02
- 拉伸強度 [MPa]: 31.0
- 熱變形溫度 [℃]: 130.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in3 | |
| Melt Flow | 42 g/10 min @Load 2.16 kg, Temperature 235 °C | 42 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 19 % | 19 % | 50 mm/min |
| Tensile Modulus | 0.570 GPa | 82.7 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | Low Temp |
| NB | NB | ||
| Charpy Impact, Notched | 1.77 J/cm2 | 8.42 ft-lb/in2 | |
| 0.410 J/cm2 @Temperature -30.0 °C | 1.95 ft-lb/in2 @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | |
| Dielectric Strength | 26.0 kV/mm | 660 kV/in | |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 120 μm/m-°C @Temperature 20.0 °C | 66.7 μin/in-°F @Temperature 68.0 °F | |
| Melting Point | 174 °C | 345 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 48.0 °C | 118 °F | |
| Vicat Softening Point | 134 °C | 273 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.10 mm | HB @Thickness 0.122 in | ||